Vulcanisable compositions based on epoxy group-containing nitrile rubbers

ABSTRACT

There are provided novel vulcanizable compositions based on optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups, specific basic crosslinkers and crosslinking accelerators, as a result of which the use of conventional crosslinkers, such as sulphur in particular, is no longer required. The vulcanizates producible therefrom possess very good compression sets at room temperature, 100° C. and 150° C., and additionally exhibit high tensile stress combined with good elongation at break.

The invention relates to vulcanizable compositions based on optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups, and specific crosslinkers, to a process for production thereof, to a process for production of vulcanizates therefrom, to the vulcanizates thus obtained, and to fully or partly hydrogenated nitrile rubbers containing epoxy groups.

Nitrile rubbers, often also abbreviated to “NBR”, are understood to mean rubbers which are co- or terpolymers of at least one α,β-unsaturated nitrile, at least one conjugated diene and optionally one or more further copolymerizable monomers. Hydrogenated nitrile rubbers (“FINER”) are understood to mean corresponding co- or terpolymers in which all or some of the C═C double bonds of the copolymerized diene units have been hydrogenated.

For many years, both NBR and HNBR have occupied an established position in the specialty elastomers sector. They possess an excellent profile of properties, in the form of excellent oil resistance, good heat stability, excellent resistance to ozone and chemicals, the latter being even more pronounced in the case of HNBR than in the case of NBR, NBR and HNBR also have very good mechanical and performance properties. For this reason, they are widely used in a wide hey variety of different fields of use, and are used, for example, for production of gaskets, hoses, belts and damping elements in the automotive sector, and also for stators, well seals and valve seals in the oil production sector, and also for numerous parts in the electrical industry, mechanical engineering and shipbuilding. A multitude of different types are commercially available, and these feature, according to the application sector, different monomers, molecular weights, polydispersities and mechanical and physical properties. As well as the standard types, there is increasing demand particularly for specialty types featuring contents of specific termonomers or particular functionalizations.

In practical use of (H)NBR rubbers, the vulcanization of the rubbers is also becoming increasingly important, i.e. particularly the crosslinker system and the vulcanization conditions. Thus, in addition to the conventional rubber crosslinking systems based on peroxides or sulphur, which have already been in existence for several decades, the last few years have seen developments of various new concepts for alternative crosslinking, Such crosslinking concepts also include polymers which, due to functional groups, are not amenable to all forms of crosslinking and crosslinking agents and therefore constitute a particular challenge.

U.S. Pat. No. 4,094,831 describes the crosslinking of co- or terpolymers of conjugated C₄-C₁₀-conjugated dienes, optionally additionally C₂-C₁₄-olefins and a monomer comprising epoxy groups, by using mono- and polyamines, mono- and polyanhydrides, and mono- and polycarboxylic acids. Acrylonitrile is not used as a monomer for preparation of these co- or terpolymers.

Polymer 46 (2005) 7632-7643 describes the preparation of glycidyl methacrylate-grafted acrylonitrile-butadiene-styrene copolymers (ABS-g-GMA) by emulsion polymerization. This ABS-g-GMA polymer is subsequently used to produce a blend with polybutylene terephthalate (PBT). Good dispersibility of the ABS-g-GMA particles in the PBT matrix is reported, and this is attributed to a reaction between the carboxyl/hydroxyl groups of the PBT chain ends and the epoxy groups of the GMA units at the interface.

WO-A-02/46254 describes functionalized quaterpolymers based on conjugated dienes, vinyl-substituted aromatic compounds, olefinically unsaturated nitriles and monomers containing hydroxyl groups or containing epoxy groups, rubber mixtures based thereon and use thereof for production of all kinds of rubber mouldings. The rubber mixtures may, according to page 8 line 27 and page 9 lines 18-19, comprise the customary crosslinkers. Examples of crosslinkers mentioned at page 9 lines 28 to 30 include, for example, elemental sulphur and sulphur donors, such as polysulphides, for example dithiocarbamates and thiuram polysulphides. It is stated in general terms that, in addition to the crosslinker, it is possible to use vulcanization accelerators (e.g. amines, guanidines, thioureas, thiazoles, thiurams, dithiocarbamates, xanthogenates and sulphonamides) (page 9 lines 25, 26). It is specified that these additives are used in customary amounts (page 9 line 21). Whether, and in what way, the compression set of corresponding mouldings at high temperatures and in the case of prolonged stress can be influenced by crosslinking systems of specific composition cannot be inferred from WO-A-2002/46254. According to the examples of WO-A-02/46254, the sulphur crosslinker is used in amounts of 1.5 parts by weight, based on 100 parts by weight of all rubbers present in the vulcanizable mixture.

JP-A-2005/120143 relates to rubbers containing repeat units of an unsaturated nitrile, of at least one acrylic ester, of an epoxy monomer, of at least one nonconjugated cyclic polyene and optionally of further unsaturated monomers, for example butadiene. Crosslinking agents specified are sulphur, organic peroxides or metal salts of aromatic or aliphatic carboxylic acids or anhydrides thereof.

European Polymer Journal 37 (2001), pages 547-557 describes glycidyl methacrylate-grafted nitrile rubbers which are used as compatibilizers in polymer mixtures. They are prepared by peroxidically initiated graft reaction of glycidyl methacrylate onto the NBR rubber.

EP-A-0 160 399 describes quaterpolymers based on a cyano-substituted alkyl (meth)acrylate, an alkyl acrylate, a crosslinkable monomer arid a further unsaturated monomer for applications particularly in the automotive sector, where a high use temperature, good stability to ozone and acidic petroleum or gasohol is required. The crosslinkable monomer used may also be a monomer comprising epoxy groups. Crosslinking agents specified in the case of unsaturated polymers include sulphur, sulphur donors or peroxides, and in the presence of epoxide groups the crosslinking thereof by polyamines and salts thereof, ammonium compounds, or in combination with conventional crosslinking systems.

Polymer 40 (1999), pages 3665-3676 describes using a specific methyl methacrylate/glycidyl methacrylate/ethyl acrylate terpolymer (MGE) to increase the compatibility of polybutylene terephthalate (PET) with acrylonitrile-butadiene-styrene terpolymers (ABS) in blends. It is stated that residual amounts of acids remaining in the ABS prepared by emulsion polymerization can lead to crosslinking reactions involving the epoxy functionalities of MGE. It is explained that nitrile and epoxide functions can form oxazolines as a subsequent reaction, or nitriles can be hydrolysed to give carboxyl groups, which can likewise react with epoxy groups. Evidence is presented that these crosslinkings have an adverse effect on the mechanical properties of the ABS and of the blend, and it is concluded, moreover, that strong acids can cause the formation of a gel or of a crosslinked network in the SAN matrix, provided that the MGE terpolymer is present.

U.S. Pat. No. 5,334,666 A describes vulcanizable elastomer compositions containing epoxy groups. These compositions comprise an elastomer containing epoxy groups arid a crosslinker system comprising (1) an organic compound having two structural elements —C(═X)—NH—C(═Y)— in which X and Y are each independently oxygen or sulphur, and (2) a quaternary compound selected from quaternary ammonium salts and quaternary phosphonium salts. The organic compound (1) is preferably a heterocyclic, aromatic or aliphatic compound. These heterocyclic compounds preferably include parabanic acid, alloxan, alloxantin, alloxan 5-oxime, barbituric acid, 5-hydroxybarbituric acid, 5-benzalbarbituric acid, 5-aminobarbituric acid, 5-hydroxyiminobarbituric acid, 5,5-diethylbarbituric acid, 5-ethyl-5-phenylbarbituric acid, 5-(1-methylbutyl)-5-(allyl)barbituric acid, 5,5-diallylbarbituric acid, isocyanuric acid and pseudouric acid, and compounds in which the oxygen in the aforementioned heterocyclic compounds has been replaced by a sulphur atom, e.g. 2,4-dithiobarbituric acid and 2-thiobarbituric acid. Preferred aromatic compounds are pyromellitic diimide, mellitic triimide and 1,4,5,8-naphthalic diimide, and the corresponding thioimides. Examples of aliphatic compounds are triuret, 1-methyltriuret, 1,1-diethyltriuret and tetrauret, and the corresponding thioureas. In example 5, a butadiene/acrylonitrile copolymer elastomer containing epoxy groups is vulcanized with the aid of a crosslinker. According to table 10 of U.S. Pat. No. 5,334,666, the crosslinkers used are mixtures of isocyanuric acid (1.8 phr) and OTMeABr (octadecyltrimethylammonium bromide) (1.6 phr), 5,5-diethylbarbituric acid (2.5 phr) and OTMeABr (1.6 phr) or of isocyanuric acid (1.8 phr) and CePyBr (cetylpyridinium bromide) (1.4 phr). According to the comparative example, exclusively 1 phr of ammonium benzoate is used as the crosslinker.

JP 01-113477 A relates to an adhesive which is obtained by adding a crosslinker (e.g. nadic methyl anhydride, i.e. methyl-5-norbornene-2,3-dicarboxylic anhydride) to a base component comprising 100 parts by weight of an epoxy resin, 1 to 40 parts by weight of a rubber which is obtained by grafting polymerizable monomers containing epoxy groups (e.g. glycidyl methacrylate) onto the rubber (e.g. acrylonitrile-butadiene copolymer), and 1 to 20 parts by weight of fine solid rubber particles, obtainable by dispersing a typically liquid or dissolved solid epoxy resin in a liquid rubber, and then vulcanizing the rubber. The use of conventional crosslinkers, such as sulphur and sulphur compounds, is described, as is the option of using thiurams, xanthogenates, thioureas, dithiocarbonates as accelerators.

US 2010/0152365 A1 discloses a carboxylic acid-modified nitrile copolymer latex which is used for production of mouldings and which, due to the absence of sulphur and a vulcanization accelerator, cannot trigger any allergic reactions and has further positive properties. As a crosslinkable unsaturated monomer, the copolymer latex may contain glycidyl (meth)acrylate. The crosslinker used may be an ionic crosslinker which does not trigger any allergic reactions. Claim 16 in US 2010/0152365 A1 specifies zinc oxide as an ionic crosslinker. US 2010/0152365 A1 does not describe, however, whether and in what way selection of a suitable crosslinker system can improve compression set at relatively high temperatures and for long stress periods.

U.S. Pat. No. 4,650,834 discloses epoxy-containing elastomer compositions which, as well as an elastomer (1) containing epoxy groups, comprise a polycarboxylic acid having at least two carboxyl groups in the molecule, (2) a quaternary compound selected from the group consisting of quaternary ammonium salts and quaternary phosphonium salts, and (3) a processing aid. The mixture of components (1) and (2) is used as a crosslinker. In example 5, a terpolymer based on butadiene, acrylonitrile and glycidyl methacrylate is vulcanized with the aid of a crosslinker system. The crosslinker system used is cetyltrimethylammonium bromide (2 phr)/tetradecanedioic acid (2.2 phr) or tetrabutylphosphonium bromide (1.5 phr)/tetradecanedioic acid (2.2 phr).

It was an object of the present invention to provide a thermally stable crosslinking system for nitrile rubbers containing epoxide groups, by virtue of which it is possible to substantially reduce or entirely avoid the use of peroxidic or sulphur-containing crosslinkers in vulcanizable compositions based on such nitrile rubbers containing epoxy groups, and to further improve compression sets at high temperatures and especially for long stress periods.

The novel crosslinking system shall avoid the disadvantages of the existing crosslinkers, be easy to introduce into the vulcanizable nitrile rubber compositions and enable a crosslinking reaction under uncomplicated conditions, without any occurrence of side reactions, for example acid-base reactions with further additives in the vulcanizable composition, for example ageing stabilizers. The crosslinkers used should have good handling qualities and should be usable equally successfully for nitrile rubbers containing epoxide groups and for hydrogenated nitrile rubbers containing epoxide groups. The thus crosslinked (H)NBR rubbers containing epoxide groups shall as far as possible have good to very good compression set values, especially at high temperatures and in long-term use, exhibit a good combination of elongation at break and tensile strength, and hence offer an alternative to or improvement over the conventional systems.

The object is achieved by a vulcanizable composition comprising

-   -   (i) at least one optionally fully or partly hydrogenated nitrile         rubber containing epoxy groups and comprising repeat units         derived from at least one conjugated diene, at least one         α,β-unsaturated nitrile and optionally one or more further         copolymerizable monomers, but not from a nonconjugated cyclic         polyene,     -   (ii) at least one Lewis and/or Brønsted base as a crosslinker,         and     -   (iii) at least one crosslinking accelerator selected from the         group consisting of thiurams, xanthogenates, thioureas,         dithiocarbamates and carbamates,         where the Lewis and/or Brønsted base (ii) must be different from         the defined group of crosslinking accelerators (iii), and also         crosslinkers other than those mentioned in (ii) are present in         the vulcanizable composition only in an amount less than 2.5         pans by weight based on 100 parts by weight of the optionally         fully or partly hydrogenated nitrile rubber (i) containing epoxy         groups, and crosslinking accelerators other than those mentioned         in (iii) are present only in an amount of less than 2.5 parts by         weight based on 100 parts by weight of the optionally fully or         partly hydrogenated nitrile rubber (i) containing epoxy groups.

The proviso that the Lewis and/or Brønsted base (ii) must be different from the defined group of crosslinking accelerators (iii) applies to all further embodiments, even if not mentioned explicitly for each case.

It has been found that, surprisingly, in the case of the inventive use of the aforementioned crosslinkers (ii) in combination with at least one crosslinking accelerator (iii) in the vulcanizable composition, thermally stable networks can be formed. The crosslinking or vulcanization is catalysed by the Lewis and/or Brønsted base(s) and the crosslinking accelerator (iii).

The amount of other crosslinkers used, for example sulphur, sulphur donors and peroxides and other crosslinking accelerators can be drastically reduced, and it may even be possible to dispense entirely therewith.

In one embodiment, the vulcanizable composition comprises

-   -   crosslinking accelerators other than those mentioned in (iii)         only in an amount of less than 2.5 parts by weight based on 100         parts by weight of the optionally fully or partly hydrogenated         nitrile rubber (i) containing epoxy groups and, at the same         time,     -   crosslinkers other than those mentioned in (ii) up to a maximum         amount of 2.3 parts by weight, preferably up to a maximum amount         of 2.25 parts by weight, more preferably up to a maximum amount         of 2 parts by weight, even more preferably up to a maximum         amount of 1.5 parts by weight, especially up to a maximum amount         of 1 part by weight, especially preferably up to a maximum         amount of 0.5 part by weight and very especially preferably up         to a maximum amount of 0.4 part by weight, also based in each         case on 100 parts by weight of the optionally fully or partly         hydrogenated nitrile rubber (i) containing epoxy groups.

In a further embodiment, the vulcanizable composition comprises

-   -   crosslinkers other than those mentioned in (ii) only in an         amount of less than 2.5 parts by weight based on 100 parts by         weight of the optionally fully or partly hydrogenated nitrile         rubber (i) containing epoxy groups and, at the same time,     -   crosslinking accelerators other than those mentioned in (iii) up         to a maximum amount of 2.3 parts by weight, preferably up to a         maximum amount of 2.25 parts by weight, more preferably up to a         maximum amount of 2 parts by weight, even more preferably up to         a maximum amount of 1.5 parts by weight, especially up to a         maximum amount of 1 part by weight, especially preferably up to         a maximum amount of 0.5 part by weight and very especially         preferably up to a maximum amount of 0.4 part by weight, also         based in each case on 100 parts by weight of the optionally         fully or partly hydrogenated nitrile rubber (i) containing epoxy         groups.

In a further embodiment, the vulcanizable composition comprises

-   -   crosslinkers other than those mentioned in (ii) only in an         amount of up to 1 part by weight based on 100 parts by weight of         the optionally fully or partly hydrogenated nitrile rubber (i)         containing epoxy groups and, at the same time,     -   crosslinking accelerators other than those mentioned in (iii) up         to a maximum amount of 2.3 parts by weight, preferably up to a         maximum amount of 2.25 parts by weight, more preferably up to a         maximum amount of 2 parts by weight, even more preferably up to         a maximum amount of 1.5 parts by weight, especially up to a         maximum amount of 1 part by weight, especially preferably up to         a maximum amount of 0.5 part by weight and very especially         preferably up to a maximum amount of 0.4 part by weight, also         based in each case on 100 parts by weight of the optionally         fully or partly hydrogenated nitrile rubber (i) containing epoxy         groups.

In a further embodiment, the vulcanizable composition comprises, based in each case on 100 parts by weight of the optionally fully or partly hydrogenated raffle rubber (i) containing epoxy groups,

-   -   crosslinkers other than those mentioned in (ii) up to a maximum         amount of 2.3 parts by weight and, at the same time,         crosslinking accelerators other than those mentioned in (iii) up         to a maximum amount of 2.3 parts by weight,     -   preferably crosslinkers other than those mentioned in (ii) up to         a maximum amount of 2.25 parts by weight and, at the same time,         crosslinking accelerators other than those mentioned in (iii) up         to a maximum amount of 2.25 parts by weight,     -   more preferably crosslinkers other than those mentioned in (ii)         up to a maximum amount of 2 parts by weight and, at the same         time, crosslinking accelerators other than those mentioned         in (iii) up to a maximum amount of 2 parts by weight,     -   even more preferably crosslinkers other than those mentioned         in (ii) up to a maximum amount of 1.5 parts by weight and, at         the same time, crosslinking accelerators other than those         mentioned in (iii) up to a maximum amount of 1.5 parts by         weight,     -   especially crosslinkers other than those mentioned in (ii) up to         a maximum amount of 1 part by weight and, at the some time,         crosslinking accelerators other than those mentioned in (iii) up         to a maximum amount of 1 part by weight,     -   especially preferably crosslinkers other than those mentioned         in (ii) up to a maximum amount of 0.5 part by weight and         crosslinking accelerators other than those mentioned in (iii) up         to a maximum amount of 0.5 part by weight,     -   very especially preferably crosslinkers other than those         mentioned in (ii) up to a maximum amount of 0.4 part by weight         and crosslinking accelerators other than those mentioned         in (iii) up to a maximum amount of 0.4 part by weight and     -   even more especially preferably absolutely no crosslinkers other         than those mentioned in (ii) and absolutely no crosslinking         accelerators other than those mentioned in (iii).

In a further embodiment of the vulcanizable composition, the sum of crosslinkers other than those mentioned in (ii) and crosslinking accelerators other than those mentioned in (iii) is at a maximum amount of 2.5 parts by weight, preferably at a maximum amount of 2.25 parts by weight, more preferably at a maximum amount of 2 parts by weight, even more preferably at a maximum amount of 1.5 parts by weight, especially at a maximum amount of 1 part by weight, especially preferably at a maximum amount of 0.5 part by weight and very especially preferably at a maximum amount of 0.4 part by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups.

All aforementioned embodiments preferred in any way, with regard to the correspondingly specified reduced maximum contents for the presence of crosslinkers other than those mentioned in (ii) and the presence of crosslinking accelerators other than those mentioned in (iii), also apply to the preferred embodiments of the vulcanizable composition which are also specified in the context of this application, having a chemically more specific definition of components (i), (ii) and/or (iii).

If the vulcanizable composition also comprises one or more rubbers other than those mentioned in (i), all aforementioned maximum amounts and the embodiments thereof preferred in any way for crosslinkers other than those mentioned in (ii) and crosslinking accelerators other than those mentioned in (iii) are based on 100 parts by weight of the sum of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups and all other rubbers present in the composition.

Compared to vulcanizable compositions not including any crosslinking accelerator (iii) aside from the crosslinker (ii), the inventive vulcanizable compositions have the advantage of leading to vulcanizates having improved, i.e. lower, compression set, especially at higher temperatures and often within shorter crosslinking times.

It is possible that the vulcanizable composition does not comprise any other crosslinker at all apart from the crosslinker(s) (ii) or any further crosslinking accelerator apart from those mentioned in (iii). In addition, it is also possible to dispense with the use of the known cocatalysts, and so heavy metal-free vulcanizates are obtainable. In one embodiment, the vulcanizable composition does not comprise any cocatalysts, more particularly any heavy metal-containing cocatalysts. In a further embodiment, the inventive vulcanizable composition does not comprise any crosslinker other than the crosslinker(s) (ii) or, at the same time, any crosslinking accelerator other than that/those mentioned in (iii), or, in addition, any cocatalysts, more particularly any heavy metal-containing cocatalysts. The crosslinking density can be controlled and adjusted within wide ranges through the proportion of epoxy groups in the nitrile rubber. The resulting vulcanizates exhibit excellent compression set values at temperatures from room temperature up to temperatures of 150° C.

In one embodiment, the nitrile rubber may also be a fully or partly hydrogenated nitrile rubber in which some or all of the C═C double bonds present in the repeat units of the nitrile rubber have been hydrogenated.

Crosslinker (ii): Lewis and/or Brønsted Base(s)

The Lewis or Brönsted bases used may be any suitable inorganic or organic bases, but these must not be selected from the list of compounds covered by the defined group of vulcanization accelerators (iii) fallen. It has been found to be useful to use Lewis bases which are electron pair donors, or Brønsted bases which are proton acceptors -and have a pK_(B) in the range from −12 to ₊13, preferably in the range from −11 to +12, more preferably in the range from −10.5 to +10, even more preferably in the range from −10 to +9,5 and especially in the range from −10 to +8.

The inventive vulcanizable composition preferably comprises, as crosslinker (ii), at least one inorganic or organic Brønsted and/or Lewis base.

Lewis Bases:

Any of the Lewis bases used which is an electron pair donor may be

-   -   (a) a transition metal or semimetal, aluminium, gallium, indium,         tin, thallium or lead in elemental form or     -   (b) an alkyl or aryl compound, ester, salt, complex or oxide of         the alkali metals, alkaline earth metals, transition metals or         semimetals, of aluminium, gallium, indium, tin, thallium, lead,         nitrogen, oxygen or phosphorus.

Any of the Lewis bases used which is an electron pair donor may preferably be

-   -   (a) a transition metal or semimetal, aluminium, indium or tin in         elemental form, or     -   (b) an alkyl or aryl compound, ester, salt, complex or oxide of         the alkali metals, alkaline earth metals, transition metals or         semimetals, of aluminium, indium, tin, nitrogen, oxygen or         phosphorus.

The Lewis base(s) used are more preferably crown ethers, especially 12-crown-4, cryptands, especially [2.2.2]-cryptand, ammonia, tetraalkylammonium salts, especially tetraalkylammonium bromides, benzyltrialkylammonium salts, tetraalkylphosphonium salts, benzyltrialkylphosphonium salts, triphenylphosphine, sodium cyanide or potassium cyanide, sodium iodide, bipyridine, phenanthroline, tetrahydrofuran, cyclooctadiene, hydrazine or diethyl ether.

Brønsted Bases:

The Brønsted base(s) used are preferably those selected from the group consisting of sulphates, sulphites, sulphides, phosphates, carbonates, substituted or unsubstituted amities, substituted or unsubstituted, aromatic or nonaromatic nitrogen-containing organic heterocycles, substituted or unsubstituted urea derivatives, guanidines and derivatives thereof, hydroxides of alkali metals or alkaline earth metals, salts of inorganic or organic sulphonic acids, carboxylic acids and phosphonic acids, the mono- or diesters thereof, and organometallic compounds of the alkali metals lithium, sodium and potassium.

Preferred carbonates are sodium carbonate, potassium carbonate, calcium carbonate and lithium carbonate.

Preferred substituted or unsubstituted amines are ammonia, triethylamine, diisopropylamine and triethanolamine.

Preferred substituted or unsubstituted, aromatic or nonaromatic nitrogen-containing organic heterocycles are pyridine, 1,8-diazabicyclo[5.4.0]undec-7-ene, 1,4-diazabicyclo[2.2.2]octane, tetramethylethylenediamine, pyrrolidine, pyrazole, piperidine, pyrrole and imidazole.

Preferred substituted or unsubstituted urea derivatives are urea, biuret, dimethylurea and N,N′-dimethylpropyleneurea.

Preferred salts of sulphonic acids are sodium alkylbenzylsulphonates especially sodium dodecylbenzylsulphonate.

Preferred salts of phosphonic acids are sodium or potassium salts of 1-hydroxyethane(1,1-diphosphonic acid), aminotrimethylenephosphonic acid and ethylenediaminetetra(methylenephosphonic acid).

Preferred salts of the carboxylic acids are sodium or potassium salts of ascorbic acid, acetic acid, propionic acid, acrylic acid, fumaric acid, maleic acid, benzoic acid, abietic acid and saturated and unsaturated fatty acids, for example stearic acid and oleic acid.

Preferred organometallic compounds of the elements lithium, sodium and potassium are sodium ethoxide, sodium methoxide, butyllithium, lithium diisopropylamide and potassium ethoxide.

Component (iii): Crosslinking Accelerator

In the vulcanizable compositions of this invention, the component (iii) used is at least one crosslinking accelerator selected from the group consisting of thiurams, xanthogenates, thioureas, dithiocarbamates and carbamates.

In a preferred embodiment, the vulcanizable composition comprises, as component (iii), at least one crosslinking accelerator selected from the group consisting of thiurams, xanthogenates, dithiocarbamates and carbamates.

Their vulcanization performance is often so rapid that they are virtually not used in conventional crosslinking systems due to their reactivity.

Useful thiurams preferably include a thiuram monosulphide, thiuram disulphide or thiuram polysulphides. Examples of preferred thiurams are tetramethylthiuram disulphide (TMTD), tetramethylthiuram monosulphide (TMTM), tetraethylthiuram disulphide (TETD), dipentamethylenethiuram tetrasulphide (DPTT), dipentamethylenethiuram hexasulphide (DPTH), dipentamethylenethiuram monosulphide (DPTM), dipentamethylenethiuram disulphide (DPTD), N,N′-diethyl-N,N′-diphenylthiuram disulphide (EPTDM) or dimethyldiphenylthiuram disulphide (MPTD).

Useful xanthogenates preferably include the alkali metal or zinc salts of the xanthogenates and the arylguanidine xanthogenates. Examples of preferred xanthogenates are arylguanidinium xanthogenates, bisxanthogenates or polyxanthogenates, zinc isopropylxanthogenate (ZIX) or the water-soluble sodium salt thereof (NaIX).

Useful thioureas preferably include ethylenethiourea (ETU), diphenylthiourea (DPTU), 1,3-di-o-tolylthiourea (DTTU) or diethylthiourea (DETU).

Useful dithiocarbamates preferably include the metal and ammonium dithiocarbamates. Examples of preferred dithiocarbamates are zinc dimethyldithiocarbamate (ZDMC), zinc diethyldithiocarbamate (ZDEC), zinc dibutyldithiocarbamate (ZDBC), zinc ethylphenyldithiocarbamate (ZEPC), zinc dibenzyldithiocarbamate (ZDBC), zinc pentamethylenedithiocarbamate (ZPD), zinc N-pentamethylenedithiocarbamate (Z5MC), zinc lupetidinedithiocarbamate (ZLD), zinc dialkyldithiophosphate (ZDT), zinc 2-ethylhexanoate (ZEH), zinc dinonyldithiocarbamate (ZNDNC), bismuth dimethyl dithiocarbamate (BIDD), nickel dibutyldithiocarbamate (NDBC), selenium diethyldithiocarbamate (SeEDC), selenium dimethyldithiocarbamate (SeDMC), sodium diethyldithiocarbamate (SEDC), tellurium diethyldithiocarbamate (TeEDC), tellurium diethyldithiocarbamate (TeDEC), sodium dimethyldithiocarbamate (SMDC), sodium dibutyldithiocarbamate (SBC) or sodium cyclohexylethyldithiocarbarmate (SHEC).

A useful carbamate is preferably hexamethylene diaminocarbamate.

Preference is given to a vulcanizable composition comprising

-   -   (i) at least one optionally fully or partly hydrogenated nitrile         rubber containing epoxy groups and comprising repeat units         derived from at least one conjugated diene, at least one         α,β-unsaturated nitrile and optionally one or more further         copolymerizable monomers, but not from a nonconjugated cyclic         polyene,     -   (ii) at least one Lewis and/or Brønsted base as a crosslinker,         and     -   (iii) at least one crosslinking accelerator selected from the         group consisting of thiurams, xanthogenates, dithiocarbamates         and carbamates,         where the Lewis and/or Brønsted base (ii) must be different from         the defined group of crosslinking accelerators and also         crosslinkers other than those mentioned in (ii) are present in         the vulcanizable composition only in an amount of less than 2.5         parts by weight based on 100 parts by weight of the optionally         fully or partly hydrogenated nitrile rubber (i) containing epoxy         groups, and crosslinking accelerators other than those mentioned         in (iii) are present only in an amount of less than 2.5 parts by         weight based on 100 parts by weight of the optionally fully or         partly hydrogenated nitrile rubber (i) containing epoxy groups.

In a preferred embodiment, the inventive vulcanizable composition comprises

-   -   (i) at least one optionally fully or partly hydrogenated nitrile         rubber containing epoxy groups and comprising repeat units         derived from at least one conjugated diene, at least one         α,β-unsaturated nitrile and optionally one or more further         copolymerizable monomers, but not from a nonconjugated cyclic         polyene,     -   (ii) at least one Lewis base selected from the group consisting         of crown ethers, cryptands, tetraalkylammonium bromides,         especially tetra-n-butylammonium bromide, triphenylphosphine and         bipyridine and/or a Brønsted base selected from the group         consisting of sodium carbonate, potassium carbonate, calcium         carbonate, lithium carbonate, triethylamine, diisopropylamine,         triethanolamine, pyridine, 1,8-diazabicyclo[5.4.0]undec-7-ene,         1,4-diazabicyclo[2.2.2]octane, tetramethylethylenediamine,         pyrrolidine, pyrazole, piperidine, pyrrole, imidazole, urea,         biuret, dimethylurea, N,N′-dimethylpropyleneurea and sodium         dodecylbenzylsulphonate as a crosslinker,     -   (iii) at least one crosslinking accelerator selected from the         group consisting of hexamethylene diaminocarbamate,         tetramethylthiuram disulphide (TMTD), tetramethylthiuram         monosulphide (TMTM), tetraethylthiuram disulphide (TETD),         dipentamethylenethiuram monosulphide (DPTM),         dipentamethylenethiuram disulphide (DPTD),         dimethyldiphenylthiuram disulphide (MPTD), arylguanidinium         xanthogenates, zinc isopropylxanthogenate (ZIX),         ethylenethiourea (ETU), diphenylthiourea (DPTU),         1,3-di-o-tolylthiourea (DTTU), diethylthiourea (DETU), zinc         dimethyldithiocarbamate (ZDMC), zinc diethyldithiocarbamate         (ZDEC), zinc dibutyldithiocarbamate (ZDBC), zinc         ethylphenyldithiocarbamate (ZEPC), zinc dibenzyldithiocarbamate         (ZDBC), zinc pentamethylenedithiocarbamate (ZPD), sodium         diethyldithiocarbamate (SEDC), sodium dimethyldithiocarbamate         (SMDC), sodium dibutyldithiocarbamate (SBC) and sodium         cyclohexylethyldithiocarbamate (SHEC),         where crosslinkers other than those mentioned in (ii) are         present in the vulcanizable composition only in an amount of         less than 2.5 parts by weight based on 100 parts by weight of         the optionally fully or partly hydrogenated nitrile rubber (i)         containing epoxy groups, and crosslinking accelerators other         than those mentioned in (iii) are present only in an amount of         less than 2.5 parts by weight based on 100 parts by weight of         the optionally fully or partly hydrogenated nitrile rubber (i)         containing epoxy groups.

The amount of the crosslinker (ii) and of the crosslinking accelerator (iii) can be selected as a function of the concentration of the epoxy groups in the nitrile rubber.

The vulcanizable composition typically comprises

-   -   (i) at least one optionally fully or partly hydrogenated nitrile         rubber containing epoxy groups and comprising repeat units         derived from at least one conjugated diene, at least one         α,β-unsaturated nitrile and optionally one or more further         copolymerizable monomers, but not from a nonconjugated cyclic         polyene, and     -   (ii) 0.01 to 30 parts by weight, preferably 0.05 to 25 parts by         weight, more preferably 0.1 to 15 parts by weight and especially         0.2 to 10 parts by weight, based in each case on 100 parts by         weight of the nitrile rubber (i), of at least one Lewis and/or         Brønsted base as a crosslinker,     -   (iii) 0.01 to 10 parts by weight, preferably 0.05 to 7.5 parts         by weight, more preferably 0.075 to 5 parts by weight and         especially 0.1 to 3 parts by weight, based in each case on 100         parts by weight of the nitrile rubber (i), of at least one         crosslinking accelerator selected from the group consisting of         thiurams, xanthogenates, thioureas, dithiocarbamates and         carbamates, preferably selected from the group consisting of         thiurams, xanthogenates, dithiocarbamates and carbamates,         where the Lewis and/or Brønsted base (ii) must be different from         the defined group of crosslinking accelerators (iii), and also         crosslinkers other than those mentioned in (ii) are present in         the vulcanizable composition only in an amount of less than 2.5         parts by weight based on 100 parts by weight of the optionally         fully or partly hydrogenated nitrile rubber (i) containing epoxy         groups, and crosslinking accelerators other than those mentioned         in (iii) are present only in an amount of less than 2.5 parts by         weight based on 100 parts by weight of the optionally fully or         partly hydrogenated nitrile rubber (i) containing epoxy groups.

According to the invention, the Lewis and/or Brønsted bases and the crosslinking accelerator (iii) are added to the optionally fully or partly hydrogenated nitrile rubber containing epoxy groups after the production thereof. The compounds are thus not those which are released or are already present in the course of production of the optionally fully or partly hydrogenated nitrile rubber, or in the course of compounding thereof, but rather bases metered in separately or the crosslinking accelerators defined. They are added to the nitrile rubber after the production thereof. This avoids partial crosslinking or partial gelation as early as in the course of production of the nitrile rubber.

Nitrile Rubber, Containing Epoxy Groups:

The optionally fully or partly hydrogenated nitrile rubbers (i) containing epoxy groups used in the inventive vulcanizable compositions may be any suitable optionally fully or partly hydrogenated nitrile rubbers which have repeat units derived from at least one conjugated diene, at least one α,β-unsaturated nitrile and optionally one or more further copolymerizable monomers, but not from a nonconjugated cyclic polyene, and contain epoxy groups.

The epoxy groups can either be applied to the nitrile rubber by subsequent grafting of compounds containing epoxy groups, or else can be derived from repeat units of a monomer containing epoxy groups additionally used in the production of the nitrile rubber.

Preference is given to using, in the inventive vulcanizable composition, optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups and comprising repeat units of at least one nitrile, of at least one conjugated diene, of at least one monomer containing epoxy groups, and optionally of one or more further copolymerizable monomers, but none of any nonconjugated cyclic polyenes.

The nitrile rubbers containing epoxy groups are typically produced by polymerizing the aforementioned monomers together to produce the nitrile rubber containing epoxy groups. This does not give a graft rubber which has been grafted with monomers containing epoxy groups, but rather a rubber in which the monomer containing epoxy groups has been incorporated into the polymer backbone in the form of repeat units in the course of polymerization.

The monomers which contain epoxy groups and are used to produce the nitrile rubbers containing epoxy groups preferably have the general formula (I)

in which

-   -   m is 0 or 1,     -   X is O, O(CR₂)_(p), (CR₂)_(p)O, C(═O)O, C(═O)O(CR₂)_(p),         C(═O)NR, (CR₂)_(p), N(R), N(R)(CR₂)_(p), P(R), P(R)(CR₂)_(p),         P(═O)(R), P(═O)(R)(CR₂)_(p), S, S(CR₂)_(p), S(═O),         S(═O)(CR₂)_(p), S(═O)₂(CR₂)_(p) or S(═O)₂, where R in these         radicals is the same or different and may be as defined for         R¹-R⁶,     -   Y represents repeat units of one or more mono- or         polyunsaturated monomers, comprising conjugated or nonconjugated         dienes, alkynes and vinyl compounds, or a structural element         which derives from polymers comprising polyethers, especially         polyalkylene glycol ethers and polyalkylene oxides,         polysiloxanes, polyols, polycarbonates, polyurethanes,         polyisocyanates, polysaccharides, polyesters and polyamides,     -   n and p are the same or different and are each in the range from         0 to 10 000,     -   R, R¹, R², R³, R⁴, R⁵ and R⁶ are the same or different and are         each H, a linear or branched, saturated or mono- or         polyunsaturated alkyl radical, a saturated or mono- or         polyunsaturated carbo- or heterocyclyl radical, aryl,         heteroaryl, arylalkyl, heteroarylalkyl, alkoxy, aryloxy,         heteroaryloxy, amino, amido, carbamoyl, alkylthio, arylthio,         sulphanyl, thiocarboxyl, sulphinyl, sulphono, sulphino,         sulpheno, sulphonic acids, sulphamoyl, hydroxyimino,         alkoxycarbonyl, F, Cl, Br, I, hydroxyl, phosphonato,         phosphinato, silyl, silyloxy, nitrile, borates, selenates,         carbonyl, carboxyl, oxycarbonyl, oxysulphonyl, oxo, thioxo,         epoxy, cyanates, thiocyanates, isocyanates, thioisocyanates or         isocyanides.

Optionally, the definitions given for the R, R¹ to R⁶ radicals and the repeat units Y of the general formula (I) are each mono- or polysubstituted.

The following radicals from the definitions for R, R¹ to R⁶ preferably have such mono- or polysubstitution: alkyl, carbocyclyl, heterocyclyl, aryl, heteroaryl, arylalkyl, heteroarylalkyl, alkoxy, aryloxy, alkylthio, arylthio, amino, amide, carbarnoyl, F, Cl, Br, I, hydroxyl, phosphonato, phosphinato, sulphanyl, thiocarboxyl, sulphinyl, sulphono, sulphino, sulpheno, sulphamoyl, silyl, silyloxy, carbonyl, carboxyl, oxycarbonyl, oxysulphonyl, oxo, thioxo, borates, selenates and epoxy. Useful substituents include—provided that chemically stable compounds are the result all definitions that R can assume. Particularly suitable substituents are alkyl, carbocyclyl, aryl, halogen, preferably fluorine, chlorine, bromine or iodine, nitrile (CN) and carboxyl.

Particular preference is given to using a monomer which contains epoxy groups and is of the general formula (I) in which X, R, R¹ to R⁶ and m are each as defined for the general formula (I), p and n are the same or different and are each in the range from 0 to 100.

Especially preferably, X, R, R¹ to R⁶ and m are each as defined above for the general formula (I) and p is in the range from 0 to 100 and n is zero. This monomer containing epoxy groups thus has the general structure (Ia)

in which

X, R, R¹ to R⁶, m and p are each as defined above for the general formula (I).

Especially preferably, a monomer is used which contains epoxy groups and is of the general formula (I), in which X, R and R¹ to R⁶ are each as defined above for the general formula (I), m is 1, p is 1 and n is zero.

Preferred examples of monomers containing epoxy groups are 2-ethylglycidyl acrylate, 2-ethylglycidyl methacrylate, 2-(n-propyl)glycidyl acrylate, 2-(n-propyl)glycidyl methacrylate, 2-(n-butyl)glycidyl acrylate, 2-(n-butyl)glycidyl methacrylate, glycidyl methacrylate, glycidylmethyl methacrylate, glycidyl acrylate, (3′,4′-epoxyheptyl)-2-ethyl acrylate, (3′,4′-epoxyheptyl)-2-ethyl methacrylate, 6′,7′-epoxyheptyl acrylate, 6′,7′-epoxyheptyl methacrylate, allyl glycidyl ether, allyl 3,4-epoxyheptyl ether, 6,7-epoxyheptyl allyl ether, vinyl glycidyl ether, vinyl 3,4-epoxyheptyl ether, 3,4-epoxyheptyl vinyl ether, 6,7-epoxyheptyl vinyl ether, o-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, p-vinylbenzyl glycidyl ether, 3-vinylcyclohexene oxide.

The monomer containing epoxy groups used is preferably a glycidyl(alkyl) acrylate. Particular preference is given to using glycidyl acrylate or glycidyl methacrylate.

In a preferred embodiment, the inventive vulcanizable composition comprises

-   -   (i) at least one optionally fully or partly hydrogenated nitrile         robber containing epoxy groups and comprising repeat units         derived from at least one conjugated diene, at least one         α,β-unsaturated nitrile, at least one monomer which contains         epoxy groups and is selected from the group consisting of         2-ethylglycidyl acrylate, 2-ethylglycidyl methacrylate,         2-(n-propyl)glycidyl acrylate, 2-(n-propyl)glycidyl         methacrylate, 2-(n-butyl)glycidyl acrylate, 2-(n-butyl)glycidyl         methacrylate, glycidyl methacrylate, glycidylmethyl         methacrylate, glycidyl acrylate, (3′,4′-epoxyheptyl)-2-ethyl         acrylate, (3′,4′-epoxyheptyl)-2-ethyl methacrylate,         6′,7′-epoxyheptyl acrylate, 6′,7′-epoxyheptyl methacrylate,         allyl glycidyl ether, allyl 3,4-epoxyheptyl ether,         6,7-epoxyheptyl allyl ether, vinyl glycidyl ether, vinyl         3,4-epoxyheptyl ether, 3,4-epoxyheptyl vinyl ether,         6,7-epoxyheptyl vinyl ether, o-vinylbenzyl glycidyl ether,         m-vinylbenzyl glycidyl ether, p-vinylbenzyl glycidyl ether and         3-vinylcyclohexene oxide, and optionally one or more further         copolymerizable monomers, but not from a nonconjugated cyclic         polyene,

(ii) at least one Lewis base selected from the group consisting of crown ethers, cryptands, tetraalkylammonium bromides, especially tetra-n-butylammonium bromide, triphenylphosphine and bipyridine and/or at least one Brønsted base selected from the group consisting of sodium carbonate, potassium carbonate, calcium carbonate, lithium carbonate, triethylamine, diisopropylamine, triethanolamine, pyridine, 1,8-diazabicyclo[5.4.0]undec-7-ene, 1,4-diazabicyclo[2.2.2]octane, tetramethylethylenediamine, pyrrolidine, pyrazole, piperidine, pyrrole, imidazole, urea, biuret, dimethylurea, N,N′-dimethylpropyleneurea and sodium dodecylbenzylsulphonate as a crosslinker,

-   -   (iii) at least one crosslinking accelerator selected from the         group consisting of hexamethylene diaminocarbamate,         tetramethylthiuram disulphide (TMTD), tetramethylthiuram         monosulphide (TMTM), tetraethylthiuram disulphide (TEM),         dipentamethylenethiuram monosulphide (DPTM),         dipentamethylenethiuram disulphide (DPTD),         dimethyldiphenylthiuram disulphide (MPTD), arylguanidinium         xanthogenates, zinc isopropylxanthogenate (ZIX),         ethylenethiourea (ETU), diphenylthiourea (DPTU),         1,3-di-o-tolylthiourea (DTTU), diethylthiourea (DETU), zinc         dimethyldithiocarbamate (ZDMC), zinc diethyldithiocarbamate         (ZDEC), zinc dibutyldithiocarbamate (ZDBC), zinc         ethylphenyldithiocarbamate (ZEPC), zinc dibenzyldithiocarbamate         (ZDBC), zinc pentamethylenedithiocarbamate (ZPD), sodium         diethyldithiocarbamate (SEDC), sodium dimethyldithiocarbamate         (SMDC), sodium dibutyldithiocarbamate (SBC) and sodium         cyclohexylethyldithiocarbamate (SHEC),         where crosslinkers other than those mentioned in (ii) are         present in the vulcanizable composition only in an amount of         less than 2.5 parts by weight, preferably only up to 1 part by         weight and more preferably only up to 0.75 part by weight, based         on 100 parts by weight of the optionally fully or partly         hydrogenated nitrile rubber (i) containing epoxy groups, and         crosslinking accelerators other than those mentioned in (iii)         are present only in an amount of less than 2.5 parts by weight,         preferably only up to 1 part by weight and more preferably only         up to 0.75 part by weight, based on 100 parts by weight of the         optionally fully or partly hydrogenated nitrile rubber (i)         containing epoxy groups.

In a particularly preferred embodiment, the inventive vulcanizable composition comprises

-   -   (i) at least one optionally fully or partly hydrogenated nitrile         rubber containing epoxy groups and comprising repeat units         derived from at least one conjugated diene, at least one         α,β-unsaturated nitrile, from glycidyl acrylate and/or glycidyl         methacrylate, and optionally one or more further copolymerizable         monomers, but not from a nonconjugated cyclic polyene,     -   (ii) at least one Lewis base selected from the group consisting         of crown ethers, cryptands, tetraalkylammonium bromides,         especially tetra-n-butylammonium bromide, and triphenylphosphine         or at least one Brønsted base selected from the group consisting         of sodium carbonate, potassium carbonate, lithium carbonate,         1,8-diazabicyclo[5.4.0]undec-7-ene,         1,4-diazabicyclo[2.2.2]octane, pyrrolidine, pyrazole, imidazole,         urea, biuret, dimethylurea, N,N′-dimethylpropyleneurea and         sodium dodecylbenzylsulphonate as a crosslinker,     -   (iii) at least one crosslinking accelerator selected from the         group consisting of hexamethylene diaminocarbamate,         tetramethylthiuram disulphide (TMTD), tetramethylthiuram         monosulphide (TMTM), tetraethylthiuram disulphide (TETD),         dipentamethylenethiuram disulphide (DPTD), zinc         isopropylxanthogenate (ZIX), ethylenethiourea (ETU),         1,3-di-o-tolylthiourea (DTTU), zinc dimethyldithiocarbamate         (ZDMC), zinc diethyldithiocarbamate (ZDEC), zinc         dibutyldithiocarbamate (ZDBC), zinc ethylphenyldithiocarbamate         (ZEPC), zinc pentamethylenedithiocarbamate (ZPD), sodium         diethyldithiocarbamate (SEDC) and sodium         cyclohexylethyldithiocarbamate (SHEC),         where crosslinkers other than those mentioned in (ii) are         present in the vulcanizable composition only in an amount of         less than 2.5 parts by weight, preferably only up to 1 part by         weight and more preferably only up to 0.75 part by weight, based         on 100 parts by weight of the optionally fully or partly         hydrogenated nitrile rubber (i) containing epoxy groups, and         crosslinking accelerators other than those mentioned in (iii)         are present only in an amount of less than 2.5 parts by weight,         preferably only up to 1 part by weight and more preferably only         up to 0.75 part by weight, based on 100 parts by weight of the         optionally fully or partly hydrogenated nitrile rubber (i)         containing epoxy groups.

Any conjugated diene may be present in the nitrile rubber containing epoxy groups. Preference is given to using (C₄-C₆) conjugated dienes. Particular preference is given to 1,2-butadiene, 1,3-butadiene, isoprene, 2,3-dimethylbutadiene, piperylene or mixtures thereof. Especially preferred are 1,3-butadiene and isoprene or mixtures thereof. Even more preferred is 1,3-butadiene.

The α,β-unsaturated nitrile used may be any known α,β-unsaturated nitrile, preference being given to (C₃-C₅)-α,β-unsaturated nitriles such as acrylonitrile, methacrylonitrile, ethacrylonitrile or mixtures thereof. Particular preference is given to acrylonitrile.

The further copolymerizable monomers used—if desired—may be, for example, aromatic vinyl monomers, preferably styrene, α-methylstyrene and vinylpyridine, fluorinated vinyl monomers, preferably fluoroethyl vinyl ether, fluoropropyl vinyl ether, o-fluoromethylstyrene, vinyl pentafluorobenzoate, difluoroethylene and tetrafluoroethylene, or else copolymerizable antiageing monomers, preferably N-(4-anilinophenyl)acrylamide, N-(4-anilinophenyl)methacrylamide, N-(4-anilinophenyl)cinnamide, N-(4-anilinophenyl)crotonamide, N-phenyl-4-(3-vinylbenzyloxy)aniline and N-phenyl-4-(4-vinylbenzyloxy)aniline, and also nonconjugated dienes, such as 4-cyanocyclohexene and 4-vinylcyclohexene, or else alkynes, such as 1- or 2-butyne.

In addition, the copolymerizable termonomers used may be monomers containing hydroxyl groups, preferably hydroxyalkyl (meth)acrylates. It is also possible to use correspondingly substituted (meth)acrylamides.

Examples of suitable hydroxyalkyl acrylate monomers are 2-hydroxyethyl (meth)acrylate, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl (meth)acrylate, 3-chloro-2-hydroxypropyl (meth)acrylate, 3-phenoxy-2-hydroxypropyl (meth)acrylate, glyceryl mono(meth)acrylate, hydroxybutyl (meth)acrylate, 3-chloro-2-hydroxypropyl (meth)acrylate, hydroxyhexyl (meth)acrylate, hydroxyoctyl (meth)acrylate, hydroxymethyl(meth)acrylamide, 2-hydroxypropyl (meth)acrylate, 3-hydroxypropyl(meth)acrylamide, di(ethylene glycol) itaconate, di(propylene glycol) itaconate, bis(2-hydroxypropyl) itaconate, bis(2-hydroxyethyl) itaconate, bis(2-hydroxyethyl) fumarate, bis(2-hydroxyethyl) maleate and hydroxymethyl vinyl ketone.

Alternatively, further copolymerizable monomers used may be copolymerizable termonomers containing carboxyl groups, for example α,β-unsaturated monocarboxylic acids, esters thereof, α,β-unsaturated dicarboxylic acids, mono- or diesters thereof or the corresponding anhydrides or amides thereof.

The α,β-unsaturated monocarboxylic acids used may preferably be acrylic acid and methacrylic acid.

It is also possible to use esters of the α,β-unsaturated monocarboxylic acids, preferably the alkyl esters and alkoxyalkyl esters thereof. Preference is given to the alkyl esters, especially C₁-C₁₈ alkyl esters, of the α,β-unsaturated monocarboxylic acids, particular preference to alkyl esters, especially C₁-C₁₈ alkyl esters of acrylic acid or of methacrylic acid, especially methyl acrylate, ethyl acrylate, propyl acrylate, n-butyl acrylate, tert-butyl acrylate, 2-ethylhexyl acrylate, n-dodecyl acrylate, methyl methacrylate, ethyl methacrylate, butyl methacrylate and 2-ethylhexyl methacrylate. Preference is also given to alkoxyalkyl esters of the α,β-unsaturated monocarboxylic acids, particular preference to alkoxyalkyl esters of acrylic acid or of methacrylic acid, especially C₂-C₁₂-alkoxyalkyl esters of acrylic acid or of methacrylic acid, even more preferably methoxymethyl acrylate, methoxyethyl (meth)acrylate, ethoxyethyl (meth)acrylate and methoxyethyl (meth)acrylate. It is also possible to use mixtures of alkyl esters, for example those mentioned above, with alkoxyalkyl esters, for example in the form of those mentioned above. It is also possible to use cyanoalkyl acrylates and cyanoalkyl methacrylates in which the number of carbon atoms in the cyanoalkyl group is 2-12, preferably α-cyanoethyl acrylate, β-cyanoethyl acrylate and cyanobutyl methacrylate. It is also possible to use hydroxyalkyl acrylates and hydroxyalkyl methacrylates in which the number of carbon atoms of the hydroxyalkyl groups is 1-12, preferably 2-hydroxyethyl acrylate, 2-hydroxyethyl methacrylate and 3-hydroxypropyl acrylate; it is also possible to use acrylates or methacrylates containing fluorine-substituted benzyl groups, preferably fluorobenzyl acrylate and fluorobenzyl methacrylate. It is also possible to use acrylates and methacrylates containing fluoroalkyl groups, preferably trifluoroethyl acrylate and tetrafluoropropyl methacrylate. It is also possible to use α,β-unsaturated carboxylic esters containing amino groups, such as dimethylaminomethyl acrylate and diethylaminoethyl acrylate.

Further copolymerizable monomers used may additionally be α,β-unsaturated dicarboxylic acids, preferably maleic acid, fumaric acid, crotonic acid, itaconic acid, citraconic acid and mesaconic acid.

It is additionally possible to use α,β-unsaturated dicarboxylic anhydrides, preferably maleic anhydride, itaconic anhydride, citraconic anhydride and mesaconic anhydride.

It is additionally possible to use mono- or diesters of α,β-unsaturated dicarboxylic acids.

These α,β-unsaturated dicarboxylic mono- or diesters may, for example, be alkyl, preferably C₁-C₁₀-alkyl, especially ethyl, n-propyl, isopropyl, n-butyl, tert-butyl, n-pentyl or n-hexyl, alkoxyalkyl, preferably C₂-C₁₂-alkoxyalkyl, more preferably C₃-C₈-alkoxyalkyl, hydroxyalkyl, preferably C₁-C₁₂-hydroxyalkyl, more preferably C₂-C₈-hydroxyalkyl, cycloalkyl, preferably C₅-C₁₂-cycloalkyl, more preferably C₆-C₁₂-cycloalkyl, alkylcycloalkyl, preferably C₆-C₁₂-alkylcycloalkyl, more preferably C₇-C₁₀-alkylcycloalkyl, aryl, preferably C₆-C₁₄-aryl mono- or diesters, where the diesters in each case may also be mixed esters.

Particularly preferred alkyl esters of C₆-C₁₂-unsaturated monocarboxylic acids are methyl (meth)acrylate, ethyl (meth)acrylate, propyl (meth)acrylate, n-butyl (meth)acrylate, t-butyl (meth)acrylate, hexyl (meth)acrylate, 2-ethylhexyl (meth)acrylate, octyl (meth)acrylate, 2-propylheptyl acrylate and lauryl (meth)acrylate. In particular, n-butyl acrylate is used.

Particularly preferred alkoxyalkyl esters of the α,β-unsaturated monocarboxylic acids are methoxyethyl (meth)acrylate, ethoxyethyl (meth)acrylate and methoxyethyl (meth)acrylate. In particular, methoxyethyl acrylate is used.

Other esters of the α,β-unsaturated monocarboxylic acids used are additionally, for example, polyethylene glycol (meth)acrylate, polypropylene glycol (meth)acrylate, N-(2-hydroxyethyl)acrylamide, N-(2-hydroxymethyl)acrylamide and urethane (meth)acrylate.

Examples of α,β-unsaturated dicarboxylic monoesters include

-   -   monoalkyl maleates, preferably monomethyl maleate, monoethyl         maleate, monopropyl maleate and mono-n-butyl maleate;     -   monocycloalkyl maleates, preferably monocyclopentyl maleate,         monocyclohexyl maleate and monocycloheptyl maleate;     -   monoalkylcycloalkyl maleates, preferably monomethylcyclopentyl         maleate and monoethylcyclohexyl maleate;     -   monoaryl maleates, preferably monophenyl maleate;     -   monobenzyl maleates, preferably monobenzyl maleate;     -   monoalkyl fumarates, preferably monomethyl fumarate, monoethyl         fumarate, monopropyl fumarate and mono-n-butyl fumarate;     -   monocycloalkyl fumarates, preferably monocyclopentyl fumarate,         monocyclohexyl fumarate and monocycloheptyl fumarate;     -   monoalkylcycloalkyl fumarates, preferably monomethylcyclopentyl         fumarate and monoethylcyclohexyl fumarate;     -   monoaryl fumarates, preferably monophenyl fumarate;     -   monobenzyl fumarates, preferably monobenzyl fumarate;     -   monoalkyl citraconates, preferably monomethyl citraconate,         monoethyl citraconate, monopropyl citraconate and mono-n-butyl         citraconate;     -   monocycloalkyl citraconates, preferably monocyclopentyl         citraconate, monocyclohexyl citraconate and monocycloheptyl         citraconate;

monoalkylcycloalkyl citraconates, preferably monomethylcyclopentyl citraconate and monoethylcyclohexyl citraconate;

-   -   monoaryl citraconates, preferably monophenyl citraconate;     -   monobenzyl citraconates, preferably monobenzyl citraconate;     -   monoalkyl itaconates, preferably monomethyl itaconate, monoethyl         itaconate, monopropyl itaconate and mono-n-butyl itaconate;     -   monocycloalkyl itaconates, preferably monocyclopentyl itaconate,         monocyclohexyl itaconate and monocycloheptyl itaconate;     -   monoalkylcycloalkyl itaconates, preferably monomethylcyclopentyl         itaconate and monoethylcyclohexyl itaconate;     -   monoaryl itaconates, preferably monophenyl itaconate;     -   monobenzyl itaconates, preferably monobenzyl itaconate;     -   monoalkyl mesaconates, preferably monoethyl mesaconate.

The α,β-unsaturated dicarboxylic diesters used may be the analogous diesters based on the aforementioned monoester groups, where the ester groups may also be chemically different groups.

Useful further copolymerizable monomers are additionally free-radically polymerizable compounds containing at least two olefinic double bonds per molecule. Examples of polyunsaturated compounds are acrylates, methacrylates or itaconates of polyols, for example ethylene glycol diacrylate, diethylene glycol dimethacrylate, triethylene glycol diacrylate, butanediol 1,4-diacrylate, propane-1,2-diol diacrylate, butane-1,3-diol dimethacrylate, neopentyl glycol diacrylate, trimethylolpropane di(meth)acrylate, trimethylolethane di(meth)acrylate, glyceryl di- and triacrylate, pentaerythrityl di-, tri- and tetraacrylate or -methacrylate, dipentaerythrityl tetra-, penta- and hexaacrylate or -methacrylate or -itaconate, sorbityl tetraacrylate, sorbityl hexamethacrylate, diacrylates or dimethacrylates of 1,4-cyclohexanediol, 1,4-dimethylolcyclohexane, 2,2-bis(4-hydroxyphenyl)propane, of polyethylene glycols or of oligoesters or oligourethanes with terminal hydroxyl groups. The polyunsaturated monomers used may also be acrylamides, for example methylenebisacrylamide, hexamethylene-1,6-bisacrylamide, diethylenetriaminetrismethacrylamide, bis(methacrylamidopropoxy)ethane or 2-acrylamidoethyl acrylate. Examples of polyunsaturated vinyl and allyl compounds are divinylbenzene, ethylene glycol divinyl ether, diallyl phthalate, allyl methacrylate, diallyl maleate, triallyl isocyanurate or triallyl phosphate.

In a preferred embodiment, the inventive vulcanizable composition comprises

-   -   (i) at least one optionally fully or partly hydrogenated nitrile         rubber containing epoxy groups and comprising repeat units         derived from a) acrylonitrile, b) 1,3-butadiene, c) at least one         monomer which contains epoxy groups and is selected from the         group consisting of 2-ethylglycidyl acrylate, 2-ethylglycidyl         methacrylate, 2-(n-propyl)glycidyl acrylate,         2-(n-propyl)glycidyl methacrylate, 2-(n-butyl)glycidyl acrylate,         2-(n-butyl)glycidyl methacrylate, glycidyl methacrylate,         glycidylmethyl methacrylate, glycidyl acrylate,         (3′,4′-epoxyheptyl)-2-ethyl acrylate,         (3′,4′-epoxyheptyl)-2-ethyl methacrylate, 6′,7′-epoxyheptyl         acrylate, 6′,7′-epoxyheptyl methacrylate, allyl glycidyl ether,         allyl 3,4-epoxyheptyl ether, 6,7-epoxyheptyl allyl ether, vinyl         glycidyl ether, vinyl 3,4-epoxyheptyl ether, 3,4-epoxyheptyl         vinyl ether, 6,7-epoxyheptyl vinyl ether, o-vinylbenzyl glycidyl         ether, m-vinylbenzyl glycidyl ether, p-vinylbenzyl glycidyl         ether and 3-vinylcyclohexene oxide, and d) optionally one or         more further copolymerizable monomers, but not from a         nonconjugated cyclic polyene,     -   (ii) at least one Lewis base selected from the group consisting         of crown ethers, cryptands, tetraalkylammonium bromides,         especially tetra-n-butylammonium bromide, and triphenylphosphine         and/or a Brønsted base selected from the group consisting of         sodium carbonate, potassium carbonate, lithium carbonate,         1,8-diazabicyclo[5.4.0]undec-7-ene,         1,4-diazabicyclo[2.2.2]octane, pyrrolidine, pyrazole, imidazole,         urea, biuret, dimethylurea, N,N′-dimethylpropyleneurea and         sodium dodecylbenzylsulphonate as a crosslinker and     -   (iii) at least one crosslinking accelerator selected from the         group consisting of hexamethylene diaminocarbamate,         tetramethylthiuram disulphide (TMTD), tetramethylthiuram         monosulphide (TMTM), tetraethylthiuram disulphide (TETD),         dipentamethylenethiuram disulphide (DPTD), zinc         isopropylxanthogenate (ZIX), ethylenethiourea (ETU),         1,3-di-o-tolylthiourea (DTTU), zinc dimethyldithiocarbamate         (ZDMC), zinc diethyldithiocarbamate (ZDEC), zinc         dibutyldithiocarbamate (ZDBC), zinc ethylphenyldithiocarbamate         (ZEPC), zinc pentamethylenedithiocarbamate (ZPD), sodium         diethyldithiocarbamate (SEDC) and sodium         cyclohexylethyldithiocarbamate (SHEC),         where crosslinkers other than those mentioned in (ii) are         present in the vulcanizable composition only in an amount less         than 2.5 parts by weight, preferably only up to 1 part by weight         and more preferably only up to 0.75 part by weight, based on 100         parts by weight of the optionally fully or partly hydrogenated         nitrile rubber (i) containing epoxy groups, and crosslinking         accelerators other than those mentioned in (iii) only in an         amount of less than 2.5 parts by weight, preferably only up to 1         part by weight and more preferably only up to 0.75 part by         weight, based on 100 parts by weight of the optionally fully or         partly hydrogenated nitrile rubber (i) containing epoxy groups.

In a preferred embodiment, the inventive vulcanizable composition comprises

-   -   (1) at least one optionally fully or partly hydrogenated nitrile         rubber containing epoxy groups and comprising repeat units         derived from a) acrylonitrile, b) 1,3-butadiene, c) glycidyl         acrylate and/or glycidyl methacrylate, and d) optionally one or         more further copolymerizable monomers, but not from a         nonconjugatecl cyclic polyene,     -   (ii) at least one Lewis base selected from the group consisting         of crown ethers, cryptands, tetraalkylammonium bromides,         especially tetra-n-butylammonium bromide, and triphenylphosphine         and/or a Brønsted base selected from the group consisting of         sodium carbonate, potassium carbonate, lithium carbonate,         1,8-diazabicyclo[5.4.0]undec-7-ene, 1,4-azabicyclo[2.2.2]octane,         pyrrolidine, pyrazole, imidazole, urea, biuret, dimethylurea,         N,N′-dimethylpropyleneurea and sodium dodecylbenzylsulphonate as         a crosslinker,     -   (iii) at least one crosslinking accelerator selected from the         group consisting of hexamethylene diaminocarbamate,         tetramethylthiuram disulphide (TMTD), tetramethylthiuram         monosulphide (TMTM), tetraethylthiuram disulphide (TETD),         dipentamethylenethiuram disulphide (DPTD), zinc         isopropylxanthogenate (ZIX), ethylenethiourea (ETU),         1,3-di-o-tolylthiourea (DTTU), zinc dimethyldithiocarbamate         (ZDMC), zinc diethyldithiocarbamate (ZDEC), zinc         dibutyldithiocarbamate (ZDBC), zinc ethylphenyldithiocarbamate         (ZEPC), zinc pentamethylenedithiocarbamate (ZPD), sodium         diethyldithiocarbamate (SEDC) and sodium         cyclohexylethyldithiocarbamate (SHEC),         where crosslinkers other than those mentioned in (ii) are         present in the vulcanizable composition only in an amount less         than 2.5 parts by weight, preferably only up to 1 part by weight         and more preferably only up to 0.75 part by weight, based on 100         parts by weight of the optionally fully or partly hydrogenated         nitrile rubber (i) containing epoxy groups, and crosslinking         accelerators other than those mentioned in (iii) are present         only in an amount of less than 2.5 parts by weight, preferably         only up to 1 part by weight and more preferably only up to 0.75         part by weight, based on 100 parts by weight of the optionally         fully or partly hydrogenated nitride rubber (i) containing epoxy         groups.

Ratios of the Monomers:

The proportions of the respective monomers in the optionally fully or partly hydrogenated nitrile rubbers which contain epoxy groups and are to be used in accordance with the invention can vary within wide ranges.

The proportion of, or of the sum of, the conjugated diene(s) is typically in the range from 39.75 to 90% by weight, preferably in the range from 44 to 88% by weight, more preferably 45.75 to 87% and especially 47.5 to 85% by weight, based on the overall nitrile rubber.

The proportion of, or of the sum of, the α,β-unsaturated nitrile(s) is typically 5 to 60% by weight, preferably 10 to 55% by weight, more preferably 13 to 53% by weight and especially 15 to 51% by weight, based on overall nitrile rubber.

The proportion of monomers containing epoxy groups is preferably 0.25 to 35% by weight, more preferably 1 to 30% by weight, more preferably 1,25 to 25% by weight and especially 1.5 to 18% by weight, based on overall nitrile rubber.

The proportions of all monomers must in each case add up to 100% by weight.

The amount of monomer containing epoxy groups in the nitrile rubber (i), the amount of the crosslinker (ii) and of the crosslinking accelerator (iii) and the ratio of epoxy groups to crosslinker (ii) and crosslinking accelerator (iii) is set according to the desired degree of crosslinking. By setting the ratio of epoxy groups to the amount of crosslinker (ii) and crosslinking accelerator (iii), it is possible to adjust the elongation at break and tensile strength to the particular requirements.

The optional further copolymerizable monomers may, according to their nature, be present in amounts of 0 to 50% by weight, based on the overall nitrile rubber (i). In this case, corresponding proportions of the conjugated diene(s) and/or of the α,β-unsaturated nitrile(s) and/or of the monomer containing epoxy groups may be replaced by the proportions of the additional monomers, where the proportions of all monomers must again in each case add up to 100% by weight.

The preparation of such optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups is sufficiently well-known to those skilled in the art. The nitrile rubber containing epoxy groups is typically prepared by what is called an emulsion polymerization. This is conducted in the presence of emulsifiers, which are typically water-soluble salts of anionic emulsifiers or else uncharged emulsifiers. In addition, polymerization is frequently effected in the presence of what are called molecular weight regulators, which are generally alkyl thiols containing 12-16 carbon atoms, preferably tert-dodecyl mercaptans (t-DDM). Such alkyl thiols or (isomer) mixtures of alkyl thiols are either commercially available or else are preparable by processes sufficiently well-described in the literature for the person skilled in the art.

To conduct the polymerization, all or individual components of the initiator system are metered in at the start of the polymerization and/or during the polymerization. Addition of all and individual components in portions during the polymerization is preferred. Sequential addition can be used to control the reaction rate. To achieve homogeneous running of the polymerization, only a portion of the initiator system is used for the start of the polymerization and the rest is metered in during the polymerization. Typically, the polymerization is commenced with 10 to 80% by weight, preferably 30-50% by weight, of the total amount of initiator. It is also possible to subsequently meter in individual constituents of the initiator system. If the intention is to prepare chemically homogeneous products, the monomers are metered in. Acrylonitrile and butadiene in particular are metered in subsequently if the composition is outside the azeotropic butadiene/acrylonitrile ratio. Preference is given to subsequent metered addition in the case of NBR types with acrylonitrile contents of 10 to 34% by weight, and in the case of the types with 40 to 50% by weight of acrylonitrile (W. Hofmann, Rubber Chem. Technol. 36 (1963). The polymerization time is in the range from 5 h to 15 h and depends particularly on the acrylonitrile content of the monomer mixture and on the polymerization temperature. The latter is in the range from 0 to 30° C., preferably in the range from 5 to 25° C. On attainment of conversions in the range from 50 to 90%, preferably in the range from 60 to 85%, the polymerization is ended, typically by adding a commonly known stopper. The amount of water used in the emulsion polymerization is in the range from 100 to 900 parts by weight, preferably in the range from 120 to 500 parts by weight and more preferably in the range from 150 to 400 parts by weight of water, based on 100 parts by weight of the monomer mixture. The polymerization can be performed either batchwise or else continuously in a stirred tank cascade. To remove unconverted monomers and volatile constituents, the “stopped” latex is subjected to a steam distillation. In this case, temperatures in the range from 70° C. to 150° C. are employed, the pressure being reduced in the case of temperatures of <100° C. Before the volatile constituents are removed, the latex can be post-stabilized with emulsifier. For this purpose, the aforementioned emulsifiers are appropriately used in amounts of 0.1 to 2.5% by weight, preferably 0.5 to 2.0% by weight, based on 100 parts by weight of nitrile rubber.

Metathesis and Hydrogenation:

It is also possible that the preparation of the nitrile rubber (a) containing epoxy groups is followed by a metathesis reaction to reduce the molecular weight of the nitrile rubber or (b) a metathesis reaction and a subsequent hydrogenation or (c) only a hydrogenation. These metathesis or hydrogenation reactions are sufficiently well-known to those skilled in the art and are described in the literature. Metathesis is known, for example, from WO-A-02/100941 and WO-A-02/100905 and can be used to reduce the molecular weight.

The hydrogenation can be performed using homogeneous or heterogeneous hydrogenation catalysts. The catalysts used are based typically on rhodium, ruthenium or titanium, but it is also possible to use platinum, iridium, palladium, rhenium, ruthenium, osmium, cobalt or copper, either as the metal or else preferably in the form of metal compounds (see, for example, U.S. Pat. No. 3,700,637, DE-A-25 39 132, EP-A-0 134 023, DE-A-35 41 689, DE-A-35 40 918, EP-A-0 298 386, DE-A-35 29 252, DE-A-34 33 392, U.S. Pat. No. 4,464,515 and U.S. Pat. No. 4,503,196).

Suitable catalysts and solvents for a hydrogenation in homogeneous phase are described hereinafter and are also known from DE-A-25 39 132 and EP-A-0 471 250. The selective hydrogenation can be achieved, for example, in the presence of a rhodium or ruthenium catalyst. It is possible to use, for example, a catalyst of the general formula

(R¹ _(m)B)_(l)MX_(n)

in which M is ruthenium or rhodium. R¹ is the same or different and is a C₁-C₈ alkyl group, a C₄-C₈ cycloalkyl group, a C₆-C₁₅ aryl group or a C₇-C₁₅ aralkyl group. B is phosphorus, arsenic, sulphur or a sulphoxide group S═O, X is hydrogen or an anion, preferably halogen and more preferably chlorine or bromine, l is 2, 3 or 4, m is 2 or 3 and n is 1, 2 or 3, preferably 1 or 3. Preferred catalysts are tris(triphenylphosphine)rhodium(I) chloride, tris(triphenylphosphine)rhodium(III) chloride and tris(dimethylsulphoxide)rhodium(I) chloride, and also tetrakis(triphenylphosphine)rhodium hydride of the formula (C₆H₅)₃P)₄RhH and the corresponding compounds in which the triphenylphosphine has been replaced fully or partly by tricyclohexylphosphine. The catalyst can be used in small amounts. An amount in the range of 0.01-1% by weight, preferably in the range of 0.03-0.5% by weight and more preferably in the range of 0.1-0.3% by weight, based on the weight of the polymer, is suitable.

It is typically advisable to use the catalyst together with a cocatalyst which is a ligand of the formula R¹ _(m)B where R¹, m and B are each as defined above for the catalyst. Preferably, in is 3, B is phosphorus and the R¹ radicals may be the same or different. The cocatalysts preferably have trialkyl, tricycloalkyl, triaryl, triaralkyl, diaryl monoalkyl, diaryl monocycloalkyl, dialkyl monoaryl, dialkyl monocycloalkyl, dicycloalkyl monoaryl or dicycloalkyl monoaryl radicals.

Examples of cocatalysts can be found, for example, in U.S. Pat. No. 4,631,315. A preferred cocatalyst is triphenylphosphine. The cocatalyst is used preferably in amounts within a range of 0.3-5% by weight, preferably in the range of 0.5-4% by weight, based on the weight of the nitrile rubber to be hydrogenated. Preferably, in addition, the weight ratio of the rhodium catalyst to the cocatalyst is in the range from 1:3 to 1:55, more preferably in the range from 1:5 to 1:45, based on 100 parts by weight of the nitrile rubber to be hydrogenated; preferably 0.1 to 33 parts by weight of the cocatalyst, more preferably 0.5 to 20 and even more preferably 1 to 5 parts by weight, especially more than 2 but less than 5 parts by weight, of cocatalyst based on 100 parts by weight of the nitrile rubber to be hydrogenated, are used.

The practical conduct of the hydrogenation is known to those skilled in the art from U.S. Pat. No. 6,683,136. It is effected typically by contacting the nitrile rubber to be hydrogenated with hydrogen in a solvent such as toluene or monochlorobenzene at a temperature in the range from 100 to 150° C. and a pressure in the range from 50 to 150 bar for 2 to 10 h.

Hydrogenation is understood in the context of this invention to mean a conversion of the double bonds present in the starting nitrile rubber to an extent of at least 50%, preferably 70-100%, more preferably 80-100%. The determination of the degree of hydrogenation is well-known to those skilled in the art and can be effected, for example, by Raman or IR spectroscopy (see, for example, EP-A-0 897 933 for the determination by Raman spectroscopy or U.S. Pat. No. 6,522,408 for the determination via IR spectroscopy).

In the case of use of heterogeneous catalysts, these are typically supported catalysts based on palladium, which are supported, for example, on charcoal, silica, calcium carbonate or barium sulphate.

This affords fully or partly hydrogenated nitrile rubbers containing epoxy groups. These have repeat units derived from at least one conjugated diene, at least one α,β-unsaturated nitrile and optionally one or more further copolymerizable monomers, but not from a nonconjugated cyclic polyene.

These optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups typically have Mooney viscosities (ML (1+4@100° C.)) in the range from 10 to 160 and preferably from 15 to 150 Mooney units, more preferably from 20 to 150 Mooney units and especially 25 to 145 Mooney units. The values of the Mooney viscosity (ML 1+4@100° C.) are determined by means of a shearing disc 2.5 viscometer to DIN 53523/3 or ASTM 1) 1646 at 100° C.

The optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups typically additionally have a polydispersity PDI→M_(w)/M_(n), where M_(w) is the weight-average and M_(n) the number-average molecular weight, in the range from 1.0 to 6.0 and preferably in the range from 1.5 to 5.0.

The glass transition temperatures of the optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups are in the range from −80° C. to +20° C., preferably in the range from −70° C. to +10° C. and more preferably in the range from −60° C. to 0° C.,

A preferred embodiment of the invention concerns vulcanizable compositions which additionally comprise (iv) at least one filler. This filler comprises exclusively compounds not already encompassed by the inventive crosslinkers (ii) or crosslinking accelerators (iii). It is possible to use, for example, carbon black, silica, carbon nanotubes, Teflon (the latter preferably in powder form) or silicates.

In further embodiments, the inventive vulcanizable compositions may also comprise one or more additives familiar to the person skilled in the art of rubber. These too are exclusively compounds not covered by the definition of the inventive crosslinkers (ii) or crosslinking accelerators (iii). These additives include filler activators, ageing stabilizers, reversion stabilizers, light stabilizers, ozone stabilizers, processing aids, plasticizers, mineral oils, tackifiers, blowing agents, dyes, pigments, waxes, resins, extenders, vulcanization retardants, and further or other additives known in the rubber industry (Ullmann's Encyclopedia of Industrial Chemistry, VCH Verlagsgesellschaft mbH, D-69451 Weinheim, 1993, vol A 23 “Chemicals and Additives”, p. 366-417).

Useful filler activators include, for example, organic silanes, preferably vinyltrimethyloxysilane, vinyldimethoxymethyl silane, vinyl triethoxysilane, vinyl tris(2-methoxyethoxy)silane, N-cyclohexyl-3-aminopropyltrimethoxysilane, 3-aminopropyltrimethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, dimethyldimethoxysilane, dimethyldiethoxysilane, trimethylethoxysilane, isooctyltrimethoxysilane, isooctyltriethoxysilane, hexadecyltrimethoxysilane or (oetadecyl)methyldimethoxysilane. Further filler activators are, for example, interface-active substances such as triethanolamine, trimethylolpropane, hexanetriol, and polyethylene glycols with molecular weights of 74 to 10 000 g/mol. The amount of filler activators is typically 0 to 10 parts by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber containing epoxide groups.

The ageing stabilizers which may be added to the vulcanizable compositions may be any of those known to those skilled in the art, which are used typically in amounts of 0 to 5 parts by weight, preferably 0.5 to 3 parts by weight, based on 100 parts by weight of the optionally hydrogenated nitrile rubber containing epoxide groups.

Useful mould release agents include, for example, saturated or partly unsaturated acids of fats and oils, and derivatives thereof (fatty acid esters, fatty acid salts, fatty alcohols, fatty acid amides). In addition, it is possible to use products applicable to the mould surface, for example products based on low molecular weight silicone compounds, products based on fluoropolymers and products based on phenol resins. The mould release agents are used in amounts of 0 to 10 parts by weight, preferably 0.5 to 5 parts by weight, based on 100 parts by weight of the optionally hydrogenated nitrile rubber containing epoxide groups.

Another possibility is reinforcement with strengthening agents (fibres) made of glass, according to the teaching of U.S. Pat. No. 4,826,721, and another is reinforcement by cords, woven fabrics, fibres made of aliphatic and aromatic polyamides (Nylon®, Aramid®), polyesters and natural fibre products.

The invention further provides the process for producing the vulcanizable compositions by mixing at least one fully or partly hydrogenated nitrile rubber (i) containing epoxy groups with at least one Lewis and/or Brønsted acid (ii) and at least one crosslinking accelerator (iii). This mixing operation can be effected in all mixing apparatuses familiar to those skilled in the art. Typically, the at least one crosslinker (ii) and the at least one crosslinking accelerator (iii) are metered into the nitrile rubber (i). When one or more fillers and one or more further rubber additives are used, they can also be mixed in in any desired sequence.

The invention further provides a process for producing vulcanizates based on an optionally fully or partly hydrogenated nitrile rubber containing epoxy groups, characterized in that the aforementioned vulcanizable composition is crosslinked with increasing temperature. The crosslinking can be effected at temperatures in the range from preferably 20 to 250° C., more preferably 50 to 230° C. The duration of the crosslinking reaction is in the range from one (1) minute to several days.

The invention also provides the vulcanizates thus obtainable. These vulcanizates contain crosslinked, optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups. They exhibit very good values in the compression set test at room temperature, 100° C. and 150° C., and additionally high tensile strength coupled with good elongations at break.

EXAMPLES

The nitrogen content for determination of the acrylonitrile content (“ACN content”) in the inventive optionally fully or partly hydrogenated nitrile rubbers containing epoxy groups is determined to DIN 53 625 according to Kjeldahl. Due to the content of polar cornonomers, the optionally hydrogenated nitrile rubbers containing epoxy groups are typically >85% by weight soluble in methyl ethyl ketone at 20° C.

The glass transition temperature and what are called the onset and offset points thereof are determined by means of Differential Scanning Calorimetry (DSC) to ASTM E 1356-03 or to DIN 11357-2.

The microstructure and the termonomer content of the individual polymers were determined by means of 1 H NMR (instrument: Bruker DPX400 with XWIN-NMR 3.1 software, measurement frequency 400 MHz, solvent CDCl3).

The values of the Mooney viscosity (ML 1+4@100° C.) are determined in each case by means of a shearing disc viscometer to DIN 53523/3 or ASTM D 1646 at 100° C. The MSR (Mooney Stress Relaxation) is determined in each case by means of a shearing disc viscometer to ISO 289-4:2003(E) at 100° C.

The vulcanization profile in the MDR and the analytical data thereof were measured on a Monsanto MDR 2000 rheometer to ASTM D5289-95.

The compression set (“CS”) at the temperature specified was measured to DIN 53517.

The Shore A hardness was measured to ASTM-D2240-81.

The tensile tests to determine stress as a function of deformation were conducted to DIN 53504 or ASTM D412-80.

The abbreviations given in the tables below have the following meanings:

-   “RT” room temperature (23±2 ° C.) -   “TS” tensile strength, measured at RT -   “EB” elongation at break, measured at RT -   “M50” modulus at 50% elongation, measured at RT -   “M100” modulus at 100% elongation, measured at RT -   “M300” modulus at 300% elongation, measured at RT -   “S min” is the minimum torque of the crosslinking isotherm -   “S max” is the maximum torque of the crosslinking isotherm -   “delta S” is “S max−S min” -   “t₁₀” is the time when 10% of S max is attained -   “t₅₀” is the time when 50% of S max is attained -   “t₉₀” is the time when 90% of S max is attained -   “t₉₅” is the time when 95% of S max is attained -   “TS2” is the time by which the Mooney viscosity has increased by two     units compared with the starting point

The following substances used in the examples:

The following chemicals were purchased as commercial products from the companies specified in each case, or originate from production plants of the companies specified.

Crosslinker (ii):

-   Lupragen® N 700 1,8-diazabicyclo-5,4,0-undecene-7 (commercial     product from BASF AG)

Crosslinking Accelerator (iii):

-   Vulkacit® P Extra N zinc ethylphenyldithiocarbamate (Lauxess     Deutschland GmbH) -   VULCOFAC® HDC hexamethylene diaminocarbamate (Safic-Alcan     Deutschland GmbH) -   RHENOCURE® SDT/S70% phosphoryl polysulfide bound to 30%     high-activity silica (Lanxess Deutschland GmbH)

Other Substances Used in the Polymerization or in the Vulcanizable Composition:

-   Corax® N550/30 carbon black (commercial product from Evonik Degussa) -   Diplast® TM 8-10/ST trioctyl mellitate (commercial product from     Lonza SpA) -   Luvomaxx® CDPA p-dicumyldiphenylamine (commercial product from     Lehmann & Voss) -   Wingstay® 29/Naugawhite mixture: mixture of 25 g of Sorbilene Mix     (mixture of Sorbitan esters and ethoxylated sorbitan esters) from     Lamberti, 38 g of Nauga-white (2,2′-methylenebis(6-nonyl-p-cresol))     from Chemtura, 125 g of Wingstay® 29 (styrenized diphenylamine) from     Eliokem and 63 g of water -   “Fe(II)SO₄ premix solution” contains 0.986 g of Fe(II)SO₄*7 H₂O and     2.0 g of Rongalit®C in 400 g of water -   Rongalit® C sodium salt of a sulphinic acid derivative (commercial     product from BASF SE) -   t-DDM tertiary dodecyl mercaptan (Lanxess Deutschland GmbH) -   Texapon® K-12 sodium laurylsulphate (commercial product from Cognis     Deutschland GmbH & Co.KG) -   Trigonox® NT 50 p-menthane hydroperoxide (commercial product from     Akzo-Degussa)

I Production of Nitrile Rubber A

Nitrile rubber A used in the example series which follow was produced according to the base formulation specified in Table 1, with all feedstocks stated in parts by weight based on 100 parts by weight of the monomer mixture. Table 1 also specifies the respective polymerization conditions.

TABLE 1 Production of nitrile rubber A Nitrile rubber A butadiene 58.5 acrylonitrile 35.5 glycidyl methacrylate (GMA) 6 Total amount of water 220 Texapon ® K-12 2.6 Na₂SO₄ 0.12 pH 7 t-DDM 0.54 Trigonox ® NT 50 0.02 Fe(II)SO₄ premix solution 0.026 diethylhydroxylamine 0.2 Wingstay ® 29/Naugawhite 0.18 Polymerization temperature [° C.] 8.0 ± 0.5 Polymerization conversion [%] 80 Polymerization time [h] 7

The nitrile rubber was produced batchwise in a 5 l autoclave with stirrer system. In the autoclave batch, 1.25 kg of the monomer mixture and a total amount of water of 2.1 kg were used, as was EDTA in an equimolar amount based on the Fe(II). 1.9 kg of this amount of water were initially charged with the emulsifier in the autoclave and purged with a nitrogen stream. Thereafter, the destabilized monomers and the amount of the t-DDM molecular weight regulator specified in Table 1 were added and the reactor was closed. After the reactor contents had been brought to temperature, the polymerizations were started by the addition of the Fe(II)SO₄ premix solution and of para-menthane hydroperoxide (Trigonox® NT50). The course of the polymerization was monitored by gravimetric determinations of conversion. On attainment of the conversion reported in Table 1, the polymerization was stopped by adding an aqueous solution of diethylhydroxylamine. Unconverted monomers and other volatile constituents were removed by means of steam distillation.

The dried NBR rubber was characterized by the Mooney viscosity, the MSR thereof, the ACN content and the glass transition temperature. The content of the termonomer was determined by ¹H NMR analysis. The solid rubber obtained had the properties reported in Tab. 2.

TABLE 2 Properties of nitrile rubber A containing epoxy groups Nitrile rubber A ACN content (%) 32.2 Mooney viscosity ML (1 + 4 at 100° C.) (Mu) 31 MSR (Mu/s) 0.671 Termonomer incorporated (% by wt.) 4.7 Glass transition temperature T_(G) (° C.) −25.1

II Production of Vulcanizates of Nitrile Rubber Terpolymer A (Comparative Example V1 and Inventive Examples V2-V4)

The nitrile rubber terpolymer A was used as described below to produce vulcanizates V1 to V4. The constituents of the vulcanizable mixtures are based on 100 parts of rubber and are reported in Tables 3 and 7.

The mixtures were produced in a Banbury Mixer. For this purpose, in each case, the rubber and all additives specified in Tables 3 and 7 were mixed at a maximum temperature of up to 120° C. for a total of 4 minutes. For this purpose, the rubber was initially charged in the mixer, all further additives were added after 1 minute, and after 2 further minutes a reversal step was conducted. After a total of 4 minutes, the rubber was discharged from the mixer. The compound was vulcanized sit the temperatures specified.

Vulcanizate V1 obtained had the properties reported in Tables 4 to 6; vulcanizates V2-V4 had the properties reported in tables 8 to 10:

TABLE 3 Composition of the vulcanizable mixture for vulcanizate V1 (Comparative Example) Vulcanizable mixture for V1 Polymer A 100 CORAX ® N 550/30 50 DIPLAST ® TM 8-10/ST 5 VULKANOX ZMB2/C5 0.4 LUVOMAXX CDPA 1 Lupragen N 700 4 Total phr 160.4 Density g/ccm 1.137

TABLE 4 Vulcanizate V1; vulcanization profile in the MDR (190° C./30 minutes) Vulcanizate V1 S max (dNm) 25.2 t₁₀ (min) 0.6 t₉₅ (min) 19.0

TABLE 5 Vulcanizate V1, properties Vulcanizate V1 Crosslinking temperature C. 190 Crosslinking time min 30 TS MPa 18.9 EB % 226 M50 MPa 2.6 M100 MPa 6.9 Hardness Shore A 71

TABLE 6 Vulcanizate V1, compression set at 23° C. and 1.50° C. Vulcanizate V1 Temperature and time: 23° C./24 hours CS % 4 Temperature and time: 150° C./24 hours CS % 33

TABLE 7 Composition of the vulcanizable mixtures for vulcanizates V2 to V4 (Inventive Examples) Vulcanizable mixture for V2 V3 V4 Polymer A 100 100 100 CORAX ® N 550/30 50 50 50 DIPLAST ® TM 8-10/ST 5 5 5 VULKANOX ZMB2/C5 0.4 0.4 0.4 LUVOMAXX CDPA 1 1 1 Lupragen N 700 4 4 4 VULKACIT P EXTRA N 1 VULCOFAC HDC 1 RHENOCURE SDT/S 1 Total phr 161.4 161.4 161.4 Density g/ccm 1.139 1.137 1.137

TABLE 8 Vulcanizates V2 to V4; vulcanization profile in the MDR (190° C./30 minutes) Vulcanizate V2 V3 V4 S max (dNm) 23.1 22.2 22.1 t₁₀ (min) 0.3 0.5 0.4 t₉₅ (min) 9.5 10.5 13.0

TABLE 9 Vulcanizates V2 to V4; properties Vulcanizate V2 V3 V4 Crosslinking ° C. 190 temperature Crosslinking time min 30 30 30 TS MPa 15.4 19.7 16.2 EB % 150 235 163 M50 MPa 3 2.4 2.8 M100 MPa 8.9 6.4 7.7 Hardness Shore A 71 69 70

TABLE 10 Vulcanizates V2 to V4; compression set as 23° C. and 150° C. Vulcanizate V2 V3 V4 Temperature and time: 23° C., 24 hours CS % 4 4 3 Temperature and time: 150° C., 24 hours CS % 24 33 24

The use of a crosslinking accelerator thus simultaneously allows the crosslinking time required to vulcanize the rubber mixtures to be shortened and surprisingly, at the same time, the long-term compression set at 150° C. to be improved. 

What is claimed is:
 1. Vulcanizable composition comprising (i) at least one optionally fully or partly hydrogenated nitrile rubber containing epoxy groups and comprising repeat units derived from at least one conjugated diene, at least one α,β-unsaturated nitrile and optionally one or more further copolymerizable monomers, but not from a nonconjugated cyclic polyene, (ii) at least one Lewis and/or Brønsted base as a crosslinker, (iii) at least one crosslinking accelerator selected from the group consisting of thiurams, xanthogenates, thioureas, dithiocarbamates and carbamates, where the Lewis and/or Brønsted base (ii) must be different from the defined group of crosslinking accelerators (iii), and also crosslinkers other than those mentioned in (ii) are present in the vulcanizable composition only in an amount of less than 2.5 parts by weight based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups, and crosslinking accelerators other than those mentioned in (iii) are present only in an amount of less than 2.5 parts by weight based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups.
 2. Vulcanizable composition according to claim 1, characterized in that it contains, based in each case on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups, crosslinkers other than those mentioned in (ii) up to a maximum amount of 2.3 parts by weight and, at the same time, crosslinking accelerators other than those mentioned in (iii) up to a maximum amount of 2,3 parts by weight, preferably crosslinkers other than those mentioned in (ii) up to a maximum amount of 2.25 parts by weight and, at the same time, crosslinking accelerators other than those mentioned in (iii) up to a maximum amount of 2.25 parts by weight, more preferably crosslinkers other than those mentioned in (ii) up to a maximum amount of 2 parts by weight and, at the same time, crosslinking accelerators other than those mentioned in (iii) up to a maximum amount of 2 parts by weight, even more preferably crosslinkers other than those mentioned in (ii) up to a maximum amount of 1.5 parts by weight and, at the same time, crosslinking accelerators other than those mentioned in (iii) up to a maximum amount of 1.5 parts by weight, especially crosslinkers other than those mentioned in (ii) up to a maximum amount of 1 part by weight and, at the same time, crosslinking accelerators other than those mentioned in (iii) up to a maximum amount of 1 part by weight, especially preferably crosslinkers other than those mentioned in (ii) up to a maximum amount of 0.5 part by weight and crosslinking accelerators other than those mentioned in (iii) up to a maximum amount of 0.5 part by weight, more especially preferably crosslinkers other than those mentioned in (ii) up to a maximum amount of 0.4 part by weight, and crosslinking accelerators other than those mentioned in (iii) up to a maximum amount of 0.4 part by weight and most especially preferably absolutely no crosslinkers other than those mentioned in (ii) and absolutely no crosslinking accelerators other than those mentioned in (iii).
 3. Vulcanizable composition according to claim 1 or 2, characterized in that the Lewis base(s) used are crown ethers, especially 12-crown-4, cryptands, especially [2.2.2]-cryptand, ammonia, tetraalkylammonium salts, especially tetraalkylammonium bromides, benzyltrialkylammonium salts, tetraalkylphosphonium salts, benzyltrialkylphosphonium salts, triphenylphosphine, sodium cyanide or potassium cyanide, sodium iodide, bipyridine, phenanthroline, tetrahydrofuran, cyclooctadiene, hydrazine or diethyl ether.
 4. Vulcanizable composition according to any of claims 1 to 3, characterized in that the Brønsted base(s) used are preferably those selected from the group consisting of sulphates, sulphites, sulphides, phosphates, carbonates, substituted or unsubstituted amines, substituted or unsubstituted, aromatic or nonaromatic nitrogen-containing organic heterocycles, substituted or unsubstituted urea derivatives, guanidines and derivatives thereof, hydroxides of alkali metals or alkaline earth metals, salts of inorganic or organic sulphonic acids, carboxylic acids and phosphonic acids, the mono- or diesters thereof, and organometallic compounds of the alkali metals lithium, sodium and potassium.
 5. Vulcanizable composition according to claim 1, comprising (i) at least one optionally fully or partly hydrogenated nitrile rubber containing epoxy groups and comprising repeat units derived from at least one conjugated diene, at least one α,β-unsaturated nitrile and optionally one or more further copolymerizable monomers, but not from a nonconjugated cyclic polyene, (ii) at least one Lewis base selected from the group consisting of crown ethers, cryptands, tetraalkylammonium bromides, especially tetra-n-butylammonium bromide, triphenylphosphine and bipyridine and/or a Brønsted base selected from the group consisting of sodium carbonate, potassium carbonate, calcium carbonate, lithium carbonate, triethylamine, diisopropylamine, triethanolamine, pyridine, 1,8-diazabicyclo[5.4.0]undec-7-ene, 1,4-diazabicyclo[2.2.2]octane, tetramethylethylenediamine, pyrrolidine, pyrazole, piperidine, pyrrole, urea, biuret, dimethylurea, N,N′-dimethylpropyleneurea and sodium dodecylbenzylsulphonate as a crosslinker, (iii) at least one crosslinking accelerator selected from the group consisting of hexamethylene diaminocarbamate, tetramethylthiuram disulphide (TMTD), tetramethylthiuram monosulphide (TMTM), tetraethylthiuram disulphide (TEM), dipentamethylenethiuram monosulphide (DP114), dipentamethylenethiuram disulphide (DPTD), dimethyldiphenylthiuram disulphide (MPTD), arylguanidinium xanthogenates, zinc isopropylxanthogenate (ZIX), ethylenethiourea (ETU), diphenylthiourea (DPTU), 1,3-di-o-tolylthiourea diethylthiourea (DETU), zinc dimethyldithiocarbamate (ZDMC), zinc diethyldithiocarbamate (ZDEC), zinc dibutyldithiocarbamate (ZDBC), zinc ethylphenyldithiocarbamate (ZEPC), zinc dibenzyldithiocarbamate (ZDBC), zinc pentamethylenedithiocarbamate (ZPD), sodium diethyldithiocarbamate (SEDC), sodium dimethyldithiocarbamate (SMDC), sodium dibutyldithiocarbamate (SBC) and sodium cyclohexylethyldithiocarbamate (SHEC), where crosslinkers other than those mentioned in (ii) are present in the vulcanizable composition only in an amount of less than 2.5 parts by weight, preferably up to 1 part by weight and more preferably up to 0.75 part by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups, and crosslinking accelerators other than those mentioned in (iii) are present only in an amount of less than 2.5 parts by weight, preferably up to 1 part by weight and more preferably up to 0.75 part by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups.
 6. Vulcanizable composition according to any of claims 1 to 5, characterized in that the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups used is one in which the epoxy groups are applied to the nitrile rubber by subsequent grafting of compounds containing epoxy groups, or else one having repeat units of at least one nitrile, of at least one conjugated diene, of at least one monomer containing epoxy groups, and optionally of one or more further copolymerizable monomers, but none of any nonconjugated cyclic polyenes.
 7. Vulcanizable composition according to any of claims 1 to 6, characterized in that the fully or partly hydrogenated nitrile rubber (i) containing epoxy groups has repeat units of a monomer which contains epoxy groups and is of the general formula (1)

in which m is 0 or 1, X is O, O(CR₂)_(p), (CR₂)_(p)O, C(═O)O, C(═O)O(CR₂)_(p), C(═O)NR, (CR₂)_(p), N(R), N(R)(CR₂)_(p), P(R), P(R)(CR₂)_(p), P(═O)(R), P(═O)(R)(CR₂)_(p), S, S(CR₂)_(p), S(═O), S(═O)(CR₂)_(p), S(═O)₂(CR₂)_(p) or S(═O)₂, where R in these radicals may be as defined for R¹-R⁶, Y represents repeat units of one or more mono- or polyunsaturated monomers, comprising conjugated or nonconjugated dienes, alkynes and vinyl compounds, or a structural element which derives from polymers comprising polyethers, especially polyalkylene glycol ethers and polyalkylene oxides, polysiloxanes, polyols, polycarbonates, polyurethanes, polyisocyanates, polysaccharides, polyesters and polyamides, n and p are the same or different and are each in the range from 0 to 10 000, R, R¹, R², R³, R⁴, R⁵ and R⁶ are the same or different and are each H, a linear or branched, saturated or mono- or polyunsaturated alkyl radical, a saturated or mono- or polyunsaturated carbo- or heterocyclyl radical, aryl, heteroaryl, arylalkyl, heteroarylalkyl, alkoxy, aryloxy, heteroaryloxy, amino, amido, carbamoyl, alkylthio, arylthio, sulphanyl, thiocarboxyl, sulphinyl, sulphono, sulphino, sulpheno, sulphonic acids, sulphamoyl, hydroxyimino, alkoxycarbonyl, F, Cl, Br, I, hydroxyl, phosphonato, phosphinato, silyl, silyloxy, nitrile, borates, selenates, carbonyl, carboxyl, oxycarbonyl, oxysulphonyl, oxo, thioxo, epoxy, cyanates, thiocyanates, isocyanates, thioisocyanates or isocyanides.
 8. Vulcanizable composition according to any of claims 1 to 7, characterized in that the fully or partly hydrogenated nitrile rubber (i) containing epoxy groups has repeat units of a monomer which contains epoxy groups and is selected from the group of 2-ethylglycidyl acrylate, 2-ethylglycidyl methacrylate, 2-(n-propyl)glycidyl acrylate, 2-(n-propyl)glycidyl methacrylate, 2-(n-butyl)glycidyl acrylate, 2-(n-butyl)glycidyl methacrylate, glycidyl methacrylate, glycidylmethyl methacrylate, glycidyl acrylate, (3′,4′-epoxyheptyl)-2-ethyl acrylate, (3′,4′-epoxyheptyl)-2-ethyl methacrylate, 6′,7′-epoxyheptyl acrylate, 6′,7′-epoxyheptyl methacrylate, allyl glycidyl ether, allyl 3,4-epoxyheptyl ether, 6,7-epoxyheptyl allyl ether, vinyl glycidyl ether, vinyl 3,4-epoxyheptyl ether, 3,4-epoxyheptyl vinyl ether, 6,7-epoxyheptyl vinyl ether, o-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, p-vinylbenzyl glycidyl ether and 3-vinylcyclohexene oxide,
 9. Vulcanizable composition according to claim 1 or 2, comprising (i) at least one optionally fully or partly hydrogenated nitrile rubber containing epoxy groups and comprising repeat units derived from a) acrylonitrile, b) 1,3-butadiene, c) at least one monomer which contains epoxy groups and is selected from the group consisting of 2-ethylglycidyl acrylate, 2-ethylglycidyl methacrylate, 2-(n-propyl)glycidyl acrylate, 2-(n-propyl)glycidyl methacrylate, 2-(n-butyl)glycidyl acrylate, 2-(n-butyl)glycidyl methacrylate, glycidyl methacrylate, glycidylmethyl methacrylate, glycidyl acrylate, (3′,4′-epoxyheptyl)-2-ethyl acrylate, (3′,4′-epoxyheptyl)-2-ethyl methacrylate, 6′,7′-epoxyheptyl acrylate, 6′,7′-epoxyheptyl methacrylate, allyl glycidyl ether, allyl 3,4-epoxyheptyl ether, 6,7-epoxyheptyl allyl ether, vinyl glycidyl ether, vinyl 3,4-epoxyheptyl ether, 3,4-epoxyheptyl vinyl ether, 6,7-epoxyheptyl vinyl ether, o-vinylbenzyl glycidyl ether, m-vinylbenzyl glycidyl ether, p-vinylbenzyl glycidyl ether and 3-vinylcyclohexene oxide, and d) optionally one or more further copolymerizable monomers, but not from a nonconjugated cyclic polyene, (ii) at least one Lewis base selected from the group consisting of crown ethers, cryptands, tetraalkylammonium bromides, especially tetra-n-butylammonium bromide, and triphenylphosphine and/or a Brønsted base selected from the group consisting of sodium carbonate, potassium carbonate, lithium carbonate, 1,8-diazabicyclo[5.4.0]undec-7-ene, 1,4-diazabicyclo[2.2,2]octane, pyrrolidine, pyrazole, imidazole, urea, biuret, dimethylurea, N,N′-dimethylpropyleneurea and sodium dodecylbenzylsulphonate as a crosslinker and (iii) at least one crosslinking accelerator selected from the group consisting of hexamethylene diaminocarbamate, tetramethylthiuram disulphide (TMTD), tetramethylthiuram monosulphide (TMTM), tetraethylthiuram disulphide (TETD), dipentamethylenethiuram disulphide (DPTD), zinc isopropylxanthogenate (ZIX), ethylenethiourea (ETU), 1,3-di-o-tolylthiourea (DTTU), zinc dimethyldithiocarbamate (ZDMC), zinc diethyldithiocarbamate (ZDEC), zinc dibutyldithiocarbamate (ZDBC), zinc ethylphenyldithiocarbamate (ZEPC), zinc pentamethylenedithiocarbamate (ZPD), sodium diethyldithiocarbamate (SEDC) and sodium cyclohexylethyldithiocarbamate (SHEC), where crosslinkers other than those mentioned in (ii) are present in the vulcanizable composition only in an amount less than 2.5 parts by weight, preferably only up to 1 part by weight and more preferably only up to 0.75 part by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups, and crosslinking accelerators other than those mentioned in (iii) only in an amount of less than 2.5 parts by weight, preferably only up to 1 part by weight and more preferably only up to 0.75 part by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups.
 10. Vulcanizable composition according to claim 1 or 2, comprising (i) at least one optionally fully or partly hydrogenated nitrile rubber containing epoxy groups and comprising repeat units derived from a) acrylonitrile, b) 1,3-butadiene, c) glycidyl acrylate and/or glycidyl methacrylate, and d) optionally one or more further copolymerizable monomers, but not from a nonconjugated cyclic polyene, (ii) at least one Lewis base selected from the group consisting of crown ethers, cryptands, tetraalkylammonium bromides, especially tetra-n-butylammonium is bromide, and triphenylphosphine and/or a Brønsted base selected from the group consisting of sodium carbonate, potassium carbonate, lithium carbonate, 1,8-diazabicyclo[5.4.0]undec-7-ene, 1,4-diazabicyclo[2.2.2]octane, pyrrolidine, pyrazole, imidazole, urea, biuret, dimethylurea, N,N′-dimethylpropyleneurea and sodium dodecylbenzylsulphonate as a crosslinker, (iii) at least one crosslinking accelerator selected from the group consisting of hexamethylene diaminocarbamate, tetramethyl thiuram disulphide (TMTD), tetramethylthiuram monosulphide (TMTM), tetraethylthiuram disulphide (TETD), dipentamethylenethiuram disulphide (DPTD), zinc isopropylxanthogenate (ZIX), ethylenethiourea (ETU), 1,3-di-o-tolylthiourea (DTTU), zinc dimethyldithiocarbamate (ZDMC), zinc diethyldithiocarbamate (ZDEC), zinc dibutyldithiocarbamate (ZDBC), zinc ethylphenyldithiocarbamate (ZEPC), zinc pentamethylenedithiocarbamate (ZPD), sodium diethyldithiocarbamate (SEDC) and sodium cyclohexylethyldithiocarbamate (SHEC), where crosslinkers other than those mentioned in (ii) are present in the vulcanizable composition only in an amount less than 2.5 parts by weight, preferably only up to 1 part by weight and more preferably only up to 0.75 part by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (i) containing epoxy groups, and crosslinking accelerators other than those mentioned in (iii) are present only in an amount of less than 2.5 parts by weight, preferably only up to 1 part by weight and more preferably only up to 0.75 part by weight, based on 100 parts by weight of the optionally fully or partly hydrogenated nitrile rubber (1) containing epoxy groups.
 11. Process for producing a vulcanizable composition according to any of claims 1 to 10 by mixing at least one fully or partly hydrogenated nitrile rubber (i) containing epoxy groups with at least one Lewis and/or Brønsted base (ii) and at least one crosslinking accelerator (iii).
 12. Process for producing vulcanizates based on an optionally fully or partly hydrogenated nitrile rubber containing epoxy groups, characterized in that the vulcanizable composition according to any of claims 1 to 10 is crosslinked with increasing temperature, preferably in the range from 20 to 250° C., more preferably in the range from 50 to 230° C.
 13. Vulcanizates based on a crosslinked, optionally fully or partly hydrogenated nitrile rubber containing epoxy groups according to any of claims 1 to
 10. 